Influencing Factors and Mechanism of Calcium Carbonate Whiskers Prepared from Calcite

Abstract

Abstract: Calcite was used as raw material, the prepared heavy magnesium water (Mg(HCO₃)₂) and the intermediate product calcium chloride were used to prepare aragonite calcium carbonate whiskers, and the products were characterized by SEM, XRD and EDS. The effects of reaction temperature, reaction time, concentration ratio of magnesium to calcium, concentration of heavy magnesium water and stirring speed on the morphology of calcium carbonate whiskers during the reaction of heavy magnesium water and calcium chloride were explored. The best process conditions are obtained through single factor experiments: temperature of 40 ℃; reaction time of 2 h; magnesium-calcium concentration ratio of 6∶1; heavy magnesium water concentration of 0.14 mol/L; stirring speed of 150 r/min. Under these conditions, aragonite calcium carbonate whiskers with a length of 40~65 μm, a diameter of 0.6~1.5 μm, and an aspect ratio of 25~45 were prepared.

Key words: calcite, heavy magnesium water, whisker, calcium carbonate

CLC Number:

YU Yajie, ZHENG Qiang, LIU Haili, XING Run, LI Xue. Influencing Factors and Mechanism of Calcium Carbonate Whiskers Prepared from Calcite[J]. JOURNAL OF SYNTHETIC CRYSTALS, 2021, 50(6): 1112-1122.

References

[1] 班建伟,刘莉,薛强.碳酸钙晶须材料的制备、应用研究进展[C]//2014年中国非金属矿科技与市场交流大会论文集.桂林,2014:18-21.
BAN J W, LIU L, XUE Q.Research progress in preparation and application of calcium carbonate whiskers[C]∥Proceedings of 2014 China Non Metallic Mineral Science and Technology and Market Exchange Conference.Guilin:2014:18-21.
[2] 曹建翠.偏钛酸为原料制备钛酸钾晶须的研究[D].镇江:江苏大学,2013.
CAO J C.Preparation of potassium titanate whiskers from metatitanic acid[D].Zhenjiang:Jiangsu University, 2013(in Chinese).
[3] 曹明莉,位建强.CaCO₃晶须研究及其在复合材料中的应用[J].化工新型材料,2010,38(8):11-13+54.
CAO M L, WEI J Q.Research progress of CaCO₃ whisker and application in composite materials[J].New Chemical Materials, 2010, 38(8):11-13+54(in Chinese).
[4] 曹有名,于德梅.碳酸钙晶须的制备[J].化工新型材料,2001,29(7):33-35.
CAO Y M, YU D M.Preparation of CaCO₃ whiskers[J].New Chemical Materials, 2001, 29(7):33-35(in Chinese).
[5] 陈沉.凝胶体系中碳酸钙晶体生长的实验研究[D].重庆:重庆大学,2006.
CHEN C.Experimental study on growth of calcium carbonate crystal in gel system[D].Chongqing:Chongqing University, 2006(in Chinese).
[6] GOMES S, RENAUDIN G, JALLOT E, et al.Structural characterization and biological fluid interaction of sol-gel-derived Mg-substituted biphasic calcium phosphate ceramics[J].ACS Applied Materials & Interfaces, 2009, 1(2):505-513.
[7] FORD J, YANG S.Directed synthesis of silica nanoparticles on micropatterned hydrogel templates tethered with poly(ethyleneimine)[J].Chemistry of Materials, 2007, 19(23):5570-5575.
[8] SOMMERDIJK N A J M, WITH G D.Biomimetic CaCO₃ mineralization using designer molecules and interfaces[J].Chemical Reviews, 2008, 108(11):4499-4550.
[9] 赵丽娜.碳酸钙的形貌控制及表面改性研究[D].长春:吉林大学,2009.
ZHAO L N.Morphology control and surface modification of calcium carbonate[D].Changchun:Jilin University, 2009(in Chinese).
[10] 闫长领,卢雁,周建国,等.高纯度高长径比CaCO₃晶须的制备[J].应用化学,2004,21(5):515-517.
YAN C L, LU Y, ZHOU J G, et al.Preparation of calcium carbonate whisker of high purity and high aspect ratio[J].Chinese Journal of Applied Chemistry, 2004, 21(5):515-517(in Chinese).
[11] 王明,丁杨,闫红旭,等.碳化法形貌可控制备碳酸钙的研究[J].无机盐工业,2018,50(12):33-36.
WANG M, DING Y, YAN H X, et al.Study on morphology-controllable synthesis of calcium carbonate in carbonization process[J].Inorganic Chemicals Industry, 2018, 50(12):33-36(in Chinese).
[12] 孙红娟,常有军.鼓泡法制备文石型碳酸钙晶须的实验研究[J].中国矿业,2005,14(2):77-79.
SUN H J, CHANG Y J.Study on preparation of aragonite style calcium carbonate whiskers[J].China Mining Magazine, 2005, 14(2):77-79(in Chinese).
[13] 陈先勇,唐琴,瞿中华,等.高长径比碳酸钙晶须的制备研究[J].河南化工,2005,22(5):16-18.
CHEN X Y, TANG Q, QU Z H, et al.Synthesis of calcium carbonate whiskers of high aspect ratios[J].Henan Chemical Industry, 2005, 22(5):16-18(in Chinese).
[14] 梁英教,车荫昌.无机物热力学数据手册[M].沈阳:东北大学出版社,1993.
LIANG Y J, CHE Y M.Handbook of inorganic thermodynamic data[M].Shenyang:Northeastern University Press, 1993(in Chinese).
[15] 李丽匣.碳酸钙晶须的制备及影响因素研究[D].沈阳:东北大学,2005.
LI L X.Study on Preparation of calcium carbonate whisker and its influencing factors[D].Shenyang:Northeastern University,2005(in Chinese).
[16] WEINSTOCK I A, ATALLA R H, REINER R S, et al.A new environmentally benign technology for transforming wood pulp into paper.Engineering polyoxometalates as catalysts for multiple processes[J].Journal of Molecular Catalysis A:Chemical, 1997, 116(1/2):59-84.
[17] RIZZUTI A, LEONELLI C.Crystallization of aragonite particles from solution under microwave irradiation[J].Powder Technology, 2008, 186(3):255-262.
[18] WANG L F, SONDI I, MATIJEVIĆ E.Preparation of uniform needle-like aragonite particles by homogeneous precipitation[J].Journal of Colloid and Interface Science, 1999, 218(2):545-553.
[19] 赵丽娜,陈璐,王悦.控制剂对文石型碳酸钙晶须合成的影响[J].吉首大学学报(自然科学版),2013,34(2):64-67.
ZHAO L N, CHEN L, WANG Y.Influence of control agent on preparation of aragonite type of calcium carbonate whisker[J].Journal of Jishou University (Natural Sciences Edition), 2013, 34(2):64-67(in Chinese).