水热反应温度对CaTi2O4(OH)2粉体微观形貌与紫外光催化性能的影响

胡其国;董伟霞;顾幸勇;罗婷;邱柏欣   

  1. 景德镇陶瓷大学材料科学与工程学院,景德镇,333403
  • 出版日期:2017-06-15 发布日期:2021-01-20
  • 基金资助:
    国家青年自然科学基金(51502119);国家自然科学基金(51462016);江西省重大自然科学基金(20152ACB21022);江西省教育厅项目(GJJ14629);科技合作领域重点项目(2016BBH80048);江西省研究生创新专项资金(YC2016-B081)

Effect of Hydrothermal Temperature on the Morphology and Ultraviolet Photocatalytic Activity of CaTi2O4(OH)2 Powders

HU Qi-guo;DONG Wei-xia;GU Xing-yong;LUO Ting;QIU Bo-xin   

  • Online:2017-06-15 Published:2021-01-20

摘要: 以钛酸正丁酯和无水氯化钙为原料,采用水热法制备了不同紫外光催化特性的CaTi2O4(OH)2粉体.利用X射线衍射仪(XRD)和扫描电子显微镜(SEM)对样品的相结构和微观形貌进行了分析,并结合粉体的紫外-可见吸收分光光谱表征了材料的吸收特性及带隙宽度.研究了不同水热反应温度对CaTi2O4(OH)2物相结构、微观形貌、晶体生长特性及紫外光催化性能的影响.结果表明:水热反应温度控制在160~200 ℃时,保温36 h都能得到纯的CaTi2O4(OH)2相,粉体的形貌随着水热反应温度的提高经历了由片状和颗粒垛堆到发育成完整的片状形貌过程,当水热反应温度在200 ℃时,片与片之间出现积聚现象;在水热反应温度为180 ℃时,制备的粉体具有最高的结晶度,在紫外光5 h下对罗丹明B的催化效率最佳.

关键词: CaTi2O4(OH)2;水热法;紫外光催化性能

Abstract: CaTi2O4(OH)2 powders with different ultraviolet photocatalytic properties were prepared by hydrothermal method using n-butyl titanate and anhydrous calcium chloride as raw materials.The phase structure, micro-morphologies, optical absorption properties and band gap width of as-prepared powders were characterized by X-Ray Diffraction(XRD), Field Emission Scanning Electron Microscope(FESEM) and UV-Vis absorption spectra(UV-Vis).The influence of different hydrothermal temperature on the phase structure, microstructure, crystal growth characteristics and ultraviolet photocatalytic properties of CaTi2O4(OH)2 were investigated.The results show that the pure CaTi2O4(OH)2 phase can be obtained at 160-200 ℃ for 36 h.The morphology of the powder from the sheet and pellet stack to develop into a complete sheet morphology process with the hydrothermal reaction temperature improved, and when the hydrothermal reaction temperature at 200 ℃, it can be found the film accumulation.The powder has the highest crystallinity when the temperature is 180 ℃, and the photocatalytic efficiency of rhodamine B is the best under UV-visible light for 5 h.

Key words: CaTi2O4(OH)2 powders with different ultraviolet photocatalytic properties were prepared by hydrothermal method using n-butyl titanate and anhydrous calcium chloride as raw materials.The phase structure, micro-morphologies, optical absorption properties and band gap width of as-prepared powders were characterized by X-Ray Diffraction(XRD), Field Emission Scanning Electron Microscope(FESEM) and UV-Vis absorption spectra(UV-Vis).The influence of different hydrothermal temperature on the phase structure, microstructure, crystal growth characteristics and ultraviolet photocatalytic properties of CaTi2O4(OH)2 were investigated.The results show that the pure CaTi2O4(OH)2 phase can be obtained at 160-200 ℃ for 36 h.The morphology of the powder from the sheet and pellet stack to develop into a complete sheet morphology process with the hydrothermal reaction temperature improved, and when the hydrothermal reaction temperature at 200 ℃, it can be found the film accumulation.The powder has the highest crystallinity when the temperature is 180 ℃, and the photocatalytic efficiency of rhodamine B is the best under UV-visible light for 5 h.