蒸氨法制备绿铜锌矿晶体的工艺研究

人工晶体学报 ›› 2024, Vol. 53 ›› Issue (4): 701-706.

蒸氨法制备绿铜锌矿晶体的工艺研究

邱诗铭^1,2,3, 闫冠杰⁴, 李春流⁴, 王胜杰^1,2,3

1.广西民族师范学院,崇左 532200;
2.广西锰资源高值化利用重点实验室,崇左 532200;
3.崇左市锰资源综合利用技术重点实验室,崇左 532200;
4.南方锰业集团有限责任公司崇左分公司,崇左 532200

收稿日期:2023-10-31 出版日期:2024-04-15 发布日期:2024-04-19
通信作者: 王胜杰,博士,高级工程师。E-mail:sjwangcn@qq.com
作者简介:邱诗铭(1983—),男,江西省人,副教授。E-mail:84323374@qq.com
基金资助:
崇左市科技计划项目(崇科20220608);广西重点研发计划(桂科AB21220027)

Process of Preparing Aurichalcite by Ammonia Distillation Method

QIU Shiming^1,2,3, YAN Guanjie⁴, LI Chunliu⁴, WANG Shengjie^1,2,3

1. Guangxi Minzu Normal University, Chongzuo 532200, China;
2. Guangxi Key Laboratory for High-Value Utilization of Manganese Resources, Chongzuo 532200, China;
3. Chongzuo Key Laboratory of Comprehensive Utilization Technology of Manganese Resources, Chongzuo 532200, China;
4. Chongzuo Branch of South Manganese Group Limited, Chongzuo 532200, China

Received:2023-10-31 Online:2024-04-15 Published:2024-04-19

摘要/Abstract

摘要： 本文以碱式碳酸铜、碱式碳酸锌和浓氨水为原料,采用蒸氨法合成绿铜锌矿。通过XRD、TGA、SEM-Mapping、FT-IR等表征手段,研究工艺条件对绿铜锌矿晶体结构的影响规律。实验表明,铜浓度为120 g/L,铜锌摩尔比分别为3∶2、1∶1、2∶3时,沉淀产物中的晶体由绿铜锌矿与孔雀石组成,且孔雀石数量随铜锌摩尔比的降低而减少。当铜锌摩尔比为2∶3,铜浓度由120 g/L降低至80 g/L时,孔雀石晶体的数量进一步减少。在铜锌摩尔比为2∶3,铜浓度为80 g/L的条件下,沉淀得到单一物相的绿铜锌矿晶体,为蒸氨法控制合成绿铜锌矿提供了数据支撑。

关键词: 蒸氨法, 工艺条件, 绿铜锌矿, 孔雀石, 晶体结构

Abstract: In this paper, aurichalcite was synthesized by ammonia distillation method, using basic copper carbonate, basic zinc carbonate and concentrated ammonia as raw materials. The effects of process conditions on the crystal structure of aurichalcite were studied by XRD, TGA, SEM-Mapping and FT-IR. It is demonstrated that when the copper concentration is fixed at 120 g/L, and the molar ratios of copper to zinc are set at 3∶2, 1∶1 and 2∶3, respectively, the crystals in the precipitation product consist of aurichalcite and malachite. As the molar ratio of copper to zinc decrease, the number of malachite crystals decrease. When the molar ratio of copper to zinc is 2∶3, a further reduction in the number of malachite crystals is observed when the copper concentration reduce from 120 g/L to 80 g/L. Finally, under the condition that the molar ratio of copper to zinc is 2∶3 and the copper concentration is 80 g/L, single-phase aurichalcite crystals are precipitated. This provides basic data for controlling the synthesis of aurichalcite by ammonia distillation method.

Key words: ammonia distillation method, process condition, aurichalcite, malachite, crystal structure

中图分类号:

TQ426

邱诗铭, 闫冠杰, 李春流, 王胜杰. 蒸氨法制备绿铜锌矿晶体的工艺研究[J]. 人工晶体学报, 2024, 53(4): 701-706.

QIU Shiming, YAN Guanjie, LI Chunliu, WANG Shengjie. Process of Preparing Aurichalcite by Ammonia Distillation Method[J]. JOURNAL OF SYNTHETIC CRYSTALS, 2024, 53(4): 701-706.

参考文献

[1] 申展, 江志东, 张鹏飞, 等. 低温甲醇水重整制氢催化剂研究进展[J]. 过程工程学报, 2022, 22(5): 573-585.
SHEN Z, JIANG Z D, ZHANG P F, et al. Progress on catalysts for hydrogen production by low temperature methanol water reforming[J]. The Chinese Journal of Process Engineering, 2022, 22(5): 573-585 (in Chinese).
[2] BEHRENS M, FURCHE A, KASATKIN I, et al. The potential of microstructural optimization in metal/oxide catalysts: higher intrinsic activity of copper by partial embedding of copper nanoparticles[J]. ChemCatChem, 2010, 2(7): 816-818.
[3] SPENCER M S. The role of zinc oxide in Cu/ZnO catalysts for methanol synthesis and the water-gas shift reaction[J]. Topics in Catalysis, 1999, 8(3): 259-266.
[4] TARASOV A, SCHUMANN J, GIRGSDIES F, et al. Thermokinetic investigation of binary Cu/Zn hydroxycarbonates as precursors for Cu/ZnO catalysts[J]. Thermochimica Acta, 2014, 591: 1-9.
[5] BEHRENS M, KIÃ NER S, GIRSGDIES F, et al. Knowledge-based development of a nitrate-free synthesis route for Cu/ZnO methanol synthesis catalystsviaformate precursors[J]. Chemical Communications, 2011, 47(6): 1701-1703.
[6] BHATTA L K G, GUNDANNA S K, MITRA A, et al. Structural and morphological aspects of transformation of aurichalcite precursor into zinc copper mixed metal oxide: an experimental investigation[J]. Materialia, 2021, 18: 101173.
[7] WILKINSON S K, VAN DE WATER L G A, MILLER B, et al. Understanding the generation of methanol synthesis and water gas shift activity over copper-based catalysts-a spatially resolved experimental kinetic study using steady and non-steady state operation under CO/CO₂/H₂ feeds[J]. Journal of Catalysis, 2016, 337: 208-220.
[8] VESBORG P C K, CHORKENDORFF I, KNUDSEN I, et al. Transient behavior of Cu/ZnO-based methanol synthesis catalysts[J]. Journal of Catalysis, 2009, 262(1): 65-72.
[9] MILLAR G J, HOLM I H, UWINS P J R, et al. Characterization of precursors to methanol synthesis catalysts Cu/ZnO system[J]. Journal of the Chemical Society, Faraday Transactions, 1998, 94(4): 593-600.
[10] REDDY B J, FROST R L, LOCKE A. Synthesis and spectroscopic characterisation of aurichalcite (Zn, Cu²⁺)₅(CO₃)₂(OH)₆; implications for Cu-ZnO catalyst precursors[J]. Transition Metal Chemistry, 2008, 33(3): 331-339.
[11] ZHENG H Y, NARKHEDE N, ZHANG H C, et al. Oriented isomorphous substitution: an efficient and alternative route to fabricate the Zn rich phase pure (Cu_1-x, Zn_x)₂(OH)₂CO₃ precursor catalyst for methanol synthesis[J]. ChemCatChem, 2020, 12(7): 2040-2049.
[12] BEHRENS M, GIRGSDIES F, TRUNSCHKE A, et al. Minerals as model compounds for Cu/ZnO catalyst precursors: structural and thermal properties and IR spectra of mineral and synthetic (zincian) malachite, rosasite and aurichalcite and a catalyst precursor mixture[J]. European Journal of Inorganic Chemistry, 2009, 2009(10): 1347-1357.
[13] LI J L, INUI T. Characterization of precursors of methanol synthesis catalysts, copper/zinc/aluminum oxides, precipitated at different pHs and temperatures[J]. Applied Catalysis A: General, 1996, 137(1): 105-117.

[1]	程佳佳, 吴梦琪, 杨敏, 王丽梅, 魏荣敏. [Co^Ⅲ(DIEN)(N₃)₃]配合物的合成、晶体结构及量子化学研究[J]. 人工晶体学报, 2024, 53(8): 1409-1415.
[2]	毛云虹, 赵春深. 6-氟-4-羟基-3-氧代-3,4-二氢喹喔啉-1(2H)-羧酸叔丁酯的合成、晶体结构及抗肿瘤活性研究[J]. 人工晶体学报, 2024, 53(7): 1257-1268.
[3]	周云龙, 宋娟, 吴苗, 任传清, 靳玲侠. 一例吡嗪基联吡啶镍配合物的合成、晶体结构及性质研究[J]. 人工晶体学报, 2024, 53(6): 1026-1033.
[4]	李波, 王霏宇, 沈红, 毛逢银, 李勇辉. 基于4-羟基间苯二甲酸和含氮杂环配体的Zn(II)配合物的合成、晶体结构与荧光性质研究[J]. 人工晶体学报, 2024, 53(4): 692-700.
[5]	林涛海, 张军, 葛庆, 张钢强, 张美丽. 基于柔性苯二乙酸Co/Ni配位聚合物的构筑和电化学性能研究[J]. 人工晶体学报, 2024, 53(3): 534-540.
[6]	张飞鹏, 路清梅, 刘卫强, 张东涛, 岳明. MnGa二元合金等静压电子结构与磁性质的研究[J]. 人工晶体学报, 2024, 53(3): 541-550.
[7]	保玉婷, 梁毅农, 孙赞. 一例锶配合物的合成、结构及表征[J]. 人工晶体学报, 2024, 53(2): 293-299.
[8]	祁金阳, 王敏, 杨瑞杰, 张迎春, 宋志国. 一种新型苯磺酸-咪唑配合物的结构及催化性能研究[J]. 人工晶体学报, 2024, 53(2): 300-306.
[9]	江涛, 梁晓彤, 廖思燕, 刘小慧, 余嘉俊, 邹霖, 邱燕璇. 基于5-氨基烟酸的锰金属有机框架的合成、结构及荧光传感性质[J]. 人工晶体学报, 2024, 53(2): 307-314.
[10]	潘会宾, 吴婷婷, 葛婧, 黄沛沛, 拓梦琪, 卢久富. 基于四核铜簇单元构筑的配位聚合物及光催化降解性能[J]. 人工晶体学报, 2024, 53(2): 315-321.
[11]	王岐, 朱晓明, 王军涛, 李泽宇, 姬柳迪, 胡鹏. 一例铽簇合物的合成、晶体结构与磁性[J]. 人工晶体学报, 2023, 52(4): 598-603.
[12]	吴淑琼, 何裕良, 郑嘉琪, 黄婉瑜, 陈培妮, 莫晓琳, 叶嘉欣, 欧晓倩, 林佳颖, 郭惠琳, 黄慧琳, 许逸戈, 史蕾, 佘婷婷, 钟永辉. 单羟基咔咯的合成、晶体的生长和光动力抗菌活性研究[J]. 人工晶体学报, 2023, 52(3): 510-519.
[13]	尹子龙, 冯光文, 陈恒雷. 不同合成方法对LiMgPO₄∶Dy发光性能的影响[J]. 人工晶体学报, 2023, 52(2): 315-321.
[14]	田娜, 刘英才, 杨远航, 肖晨希, 朱建宇, 段博峰, 张强, 宋娟. 一例吡嗪羧酸镉配合物的合成、结构及荧光性质研究[J]. 人工晶体学报, 2023, 52(2): 322-326.
[15]	余中, 王玉雪, 代平, 韩晶, 王琰, 张绪. 基于4,4'-偶氮苯二甲酸的金属-有机框架合成及其荧光性质[J]. 人工晶体学报, 2023, 52(11): 2024-2033.