Effect of Chitosan on Color Fastness of SiO2@PDA Photonic Crystals

Abstract

Abstract: The purpose of this paper is to obtain a coating structure with stable structure and bright color on the silk substrate. Monodisperse SiO₂@PDA microspheres were used as the precursor to construct SiO₂@PDA photonic crystals on the silk. The effect of chitosan solution with different mass fraction of chitosan on the color fastness of structured colored silk was investigated. The microstructure of SiO₂@PDA photonic crystals was observed by field emission scanning electron microscopy (SEM), the elemental composition of SiO₂ microspheres was characterized by energy dispersive spectroscopy (EDS), the phase structure of SiO₂ and SiO₂@PDA microspheres was characterized by X-ray diffraction, and the color fastness of structural colored silk was investigated by friction test and washing test. The results show that the SiO₂ and SiO₂@PDA microspheres prepared in this experiment have uniform particle size and good monodispersity. The structures of SiO₂@PDA photonic crystals are closely and periodically arranged. Compared with the structural colored fabric which has not been treated with chitosan solution, the structure color of the fabric treated with 3% (mass fraction) chitosan solution has less shedding after tribological test and water washing test, and still keep its original color. The results show that chitosan solution treatment can improve the color fastness of colored fabric effectively.

Key words: photonic crystal, SiO₂@PDA, structural color, chitosan, color fastness, silk

CLC Number:

O734
TS190.1

ZHANG Fei, YANG Hui. Effect of Chitosan on Color Fastness of SiO₂@PDA Photonic Crystals[J]. Journal of Synthetic Crystals, 2023, 52(10): 1766-1772.

References

[1] ZOLLINGER H. Color chemistry: syntheses, properties, and applications of organic dyes and pigments[M]. 3rd ed. Weinheim: VCH, 1991.
[2] HUNGER K. Industrial dyes: chemistry, properties, applications[M]. Weinheim: Wiley, 2002.
[3] LI Y Z, LU Z H, YIN H W, et al. Structural origin of the brown color of barbules in male peacock tail feathers[J]. Physical Review E, Statistical, Nonlinear, and Soft Matter Physics, 2005, 72(1): 010902.
[4] CHEN F X, HUANG Y, LI R, et al. Bio-inspired structural colors and their applications[J]. Chemical Communications, 2021, 57(99): 13448-13464.
[5] CHUNG K, YU S, HEO C J, et al. Flexible, angle-independent, structural color reflectors inspired by morpho butterfly wings[J]. Advanced Materials, 2012, 24(18): 2375-2379.
[6] 刘锋. 甲虫的结构色与结构变色研究[D]. 上海: 复旦大学, 2008.
LIU F. Study on structural color and structural discoloration of beetles[D].Shanghai: Fudan University, 2008 (in Chinese).
[7] 李义臣. 柔性纺织基材表面结构生色光子晶体的稳定性及快速大面积组装研究[D]. 杭州: 浙江理工大学, 2021.
LI Y C. Study on stability and rapid large-area assembly of chromophoric photonic crystals with flexible textile substrate surface structure[D].Hangzhou: Zhejiang Sci-Tech University, 2021 (in Chinese).
[8] 张慧, 刘晓艳. 光子晶体在织物表面的色泽呈现[J]. 纺织学报, 2017, 38(8): 91-95.
ZHANG H, LIU X Y. Color development of photonic crystals on fabric surface[J]. Journal of Textile Research, 2017, 38(8): 91-95 (in Chinese).
[9] ZHANG H, LIU X Y. Preparation and self-assembly of photonic crystals on polyester fabrics[J]. Iranian Polymer Journal, 2017, 26(2): 107-114.
[10] 张慧. 单分散SiO₂胶体颗粒在织物表面的色泽呈现[D]. 上海: 东华大学, 2017.
ZHANG H. Color appearance of monodisperse SiO₂ colloidal particles on fabric surface[D]. Shanghai: Donghua University, 2017 (in Chinese).
[11] ZHOU L, WU Y J, CHAI L Q, et al. Study on the formation of three-dimensionally ordered SiO₂ photonic crystals on polyester fabrics by vertical deposition self-assembly[J]. Textile Research Journal, 2016, 86(18): 1973-1987.
[12] 袁伟. 结构色纤维/面料的制备及其光学性质研究[D]. 苏州: 苏州大学, 2014.
YUAN W. Preparation and optical properties of structured color fiber/fabric[D]. Suzhou: Soochow University, 2014 (in Chinese).
[13] CUI Y, WANG F, ZHU J F, et al. Preparation of large-scale and angle-independent structural colors by additive of black polypyrrole[J]. Journal of Colloid and Interface Science, 2018, 531: 609-617.
[14] 崔云. SiO₂基非晶光子晶体结构色材料的研究[D]. 西安: 陕西科技大学, 2019.
CUI Y. Study on structural color materials of amorphous photonic crystals based on SiO₂[D]. Xi’an: Shaanxi University of Science & Technology, 2019 (in Chinese).
[15] LIU P M, CHEN J L, ZHANG Z X, et al. Bio-inspired robust non-iridescent structural color with self-adhesive amorphous colloidal particle arrays[J]. Nanoscale, 2018, 10(8): 3673-3679.
[16] 刘盼苗. 聚多巴胺修饰的纳米粒子合成及组装[D]. 南京: 东南大学, 2018.
LIU P M. Synthesis and assembly of dopamine modified nanoparticles[D]. Nanjing: Southeast University, 2018 (in Chinese).
[17] 高雅芳. 纺织基材上高稳定性光子晶体生色结构的快速制备及其性能研究[D]. 杭州: 浙江理工大学, 2021.
GAO Y F. Rapid preparation and properties of high stability photonic crystal chromophoric structure on textile substrate[D]. Hangzhou: Zhejiang Sci-Tech University, 2021 (in Chinese).
[18] 郑宏亮. 基于聚多巴胺结构生色纺织材料的制备及其显色性能研究[D]. 芜湖: 安徽工程大学, 2020.
ZHENG H L. Preparation and color-developing properties of color-developing textile materials based on poly-dopamine structure[D]. Wuhu: Anhui Polytechnic University, 2020 (in Chinese).
[19] AATCC. Test method 61-2013 colorfastness to laundering: accelerated[S]. Aatcc Technical Manual, 2015.

Effect of Chitosan on Color Fastness of SiO₂@PDA Photonic Crystals

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	WANG Zhiqiang, ZHANG Qi, LIANG Ying, WANG Wenxin, CHEN Qi. Fast Preparation of Fe₃O₄@C Photonic Crystal Flexible Composite Films by Magnetic Field Assisted Method [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2025, 54(1): 49-58.
[2]	WU Zhenyu, JIA Mengmeng, HOU Xiaohan, LIU Fucheng, FAN Weili. Band Gap Characteristics of h-BN Superlattice Plasma Photonic Crystals [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2023, 52(2): 252-260.
[3]	WANG Liqun, YAN Jiaxin, LU Xin, SHI Liwei, ZHANG Xiaoli. Multi-Component Defect State of Photonic Crystals [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2022, 51(6): 986-995.
[4]	WANG Danyan, LI Moxin, LU Rusi, ZHANG Cheng. Multilayer Thin Film Based Structural Color Filters: Principle, Fabrication and Applications [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2021, 50(7): 1287-1306.
[5]	WANG Zuhua, LIU Ping, YANG Ruixian, CHEN Huajun. Synthesis of Ag-Chitosan by Green Route and Its Isotherms, Kinetic and Antimicrobial Activity [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2021, 50(12): 2307-2315.
[6]	WANG Xiaomei, WANG Zhao, HAO Lingyun, ZHANG Xiaojuan, LIU Chu. Construction and Application of Structural Color Contact Lenses Based on Photonic Crystals [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2021, 50(11): 2164-2172.
[7]	ZHU Yu-guang;SUN Wen-wen;FANG Yun-tuan. Polarization Switch Based on Graphene Metamaterial [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2017, 46(5): 926-930.
[8]	WU Yuan-ting;LI Meng-long;YUAN Jun;LU Jian;WU Peng-hong;LIU Chang-qing;WANG Xiu-feng. Self-assembly and Stability of SiO2 Binary Photonic Crystals [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2017, 46(10): 1984-1987.
[9]	XU Jing-jing;CHEN Xi-liang;YIN Yan-ting;WU Si-yu;CHEN Qiang-guo;CHEN Qing-hua. Research on Preparation and Performance of Magnetic Modified HAP/CS/SiO2 Bone Tissue Engineering Scaffolds [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2016, 45(6): 1683-1690.
[10]	LIU Qi-neng;LIU Qin. A New Method for Study on Optical Tamm State in M-PC-M [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2016, 45(5): 1241-1247.
[11]	GUO Hou-yong;LIU Xun;PEI Chong-hua. Formation of Calcium Carbonate with Core-shell Structure Induced by Chitosan Hydrochloride [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2016, 45(5): 1357-1364.
[12]	FENG Jian-yu;DONG Li-fang;WEI Ling-yan. Investigation on the Spectrum of Self-Organized Plasma Photonic Crystal [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2016, 45(2): 328-332.
[13]	LI Wen-sheng;ZHANG Qin;HUANG Hai-ming;FU Yan-hua. Design of Haze Detector Based on Photonic Crystals [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2015, 44(9): 2614-2618.
[14]	CHEN Min;YANG Liu-chun;ZHU Li-feng;ZHANG Jun-feng;HUANG Yan. Study on Preparation of Hg Adsorbent with Modified Calcium Sulfate Whisker [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2015, 44(7): 1951-1956.
[15]	CHEN Yi;WANG Tong-biao;LIU Nian-hua;LIU Jiang-tao. Influence of Detuning on Faraday Rotation of Graphene Embedded in a Microcavity [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2015, 44(7): 1799-1805.