Luminescent Properties of LuGG∶Ce Nanophosphor  Synthesized via Co-Precipitation Method

JOURNAL OF SYNTHETIC CRYSTALS ›› 2021, Vol. 50 ›› Issue (2): 325-330.

• Research Articles • Previous Articles Next Articles

Luminescent Properties of LuGG∶Ce Nanophosphor Synthesized via Co-Precipitation Method

LIU Wenpeng¹, REN Hao², LI Hongyuan², DING Shoujun^1,2, ZHANG Qingli¹

1.The Key Laboratory of Photonic Devices and Materials, Anhui Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Hefei 230031, China;
2.School of Science and Engineering of Mathematics and Physics, Anhui University of Technology, Maanshan 243032, China

Received:2020-11-09 Published:2021-03-24
Contact: DING Shoujun, doctor, assistant professor. E-mail: sjding@ahut.edu.cn
About author:LIU Wenpeng(1981—), male, from Hebei Province, doctor, assistant professor. E-mail: Wpliu@aiofm.ac.cn
Supported by:
The Joint Fund of Chinese Academy of Sciences (6141A01080302); National Key Research and Development Program of China (2016YFB0402101); University Natural Science Research Project of Anhui Province of China (KJ2019ZD06); National Natural Science Foundation of China (51702322, 51802307); Fund of Key Laboratory of Optoelectronic Materials Chemistry and Physics, Chinese Academy of Sciences (2008DP173016)

Abstract

Abstract: Ce³⁺ doped Lu₃Ga₅O₁₂ (LuGG∶Ce) nanophosphor was synthesized via co-precipitation method. Its structured parameters were obtained by Rietveld refinement method. The morphology of the as-synthesized nanophosphor was determined with Scanning Electron Microscope (SEM). Under 365 nm excitation, the emission spectrum exhibits an asymmetry broad band with central wavelength at 438 nm and this broad band can be deconvolved into two peaks with wavelength centers at around 426 nm and 470 nm, respectively. The chromaticity coordinate of LuGG∶Ce is (0.176 9, 0.180 3), which corresponds to blue light emission. The results show LuGG∶Ce is suitable for realizing blue light emission under UV excitation and thus has potential applications in the fields of UV-excited white light emitting diodes(LEDs).

Key words: LuGG∶Ce, nanophosphor, co-precipitation method, UV excitation, white LED, luminescent property

CLC Number:

TQ422⁺.2

LIU Wenpeng, REN Hao, LI Hongyuan, DING Shoujun, ZHANG Qingli. Luminescent Properties of LuGG∶Ce Nanophosphor Synthesized via Co-Precipitation Method[J]. JOURNAL OF SYNTHETIC CRYSTALS, 2021, 50(2): 325-330.

References

[1] HUSSAIN T, ZHONG L, DANESH M, et al. Enabling low amounts of YAG∶Ce³⁺ to convert blue into white light with plasmonic Au nanoparticles[J]. Nanoscale, 2015, 7(23): 10350-10356.
[2] XIA G D, ZHOU S M, ZHANG J J, et al. Structural and optical properties of YAG∶Ce³⁺ phosphors by sol-gel combustion method[J]. Journal of Crystal Growth, 2005, 279(3/4): 357-362.
[3] KIM M, KIM H J, CHO J Y, et al. Crystal growth and scintillation properties of YAG∶Ce³⁺ for γ and α detection[J]. Applied Radiation and Isotopes, 2019, 145: 126-130.
[4] KAMADA K, NIKL M, KUROSAWA S, et al. Co-doping effects on luminescence and scintillation properties of Ce doped Lu₃Al₅O₁₂ scintillator[J]. Nuclear Instruments and Methods in Physics Research Section A: Accelerators, Spectrometers, Detectors and Associated Equipment, 2015, 782: 9-12.
[5] MOSZY$\acute{И}$SKI M, LUDZIEJEWSKI T, WOLSKI D, et al. Properties of the YAG∶Ce scintillator[J]. Nuclear Instruments and Methods in Physics Research Section A: Accelerators, Spectrometers, Detectors and Associated Equipment, 1994, 345(3): 461-467.
[6] OGIEGLO J M, ZYCH A, IVANOVSKIKH K V, et al. Luminescence and energy transfer in Lu₃Al₅O₁₂ scintillators co-doped with Ce³⁺ and Tb³⁺. The Journal of Physical Chemistry, 2012, 116: 8464-8474.
[7] OGIEGŁO J M, ZYCH A, JÜSTEL T, et al. Luminescence and energy transfer in Lu₃Al₅O₁₂ scintillators co-doped with Ce³⁺ and Pr³⁺[J]. Optical Materials, 2013, 35(3): 322-331.
[8] HU Q S, DENG Z Z, HU M C, et al. X-ray scintillation in lead-free double perovskite crystals[J]. Science China Chemistry, 2018, 61(12):1581-1586.
[9] HAUTEFEUILLE B, LEBBOU K, DUJARDIN C, et al. Shaped crystal growth of Ce³⁺-doped Lu_2(1-x)Y_2-xSiO₅ oxyorthosilicate for scintillator applications by pulling-down technique[J]. Journal of Crystal Growth, 2006, 289(1):172-177.
[10] LEMPICKI A, BERMAN E, WOJTOWICZ A J, et al. Cerium-doped orthophosphates: new promising scintillators[C]//IEEE Transactions on Nuclear Science. IEEE,: 384-387.
[11] KUCERA M, NITSCH K, KUBOVA M, et al. Ce-doped YAG and LuAG epitaxial films for scintillation detectors[J]. IEEE Transactions on Nuclear Science, 2008, 55(3): 1201-1205.
[12] MIHÓKOVÁ E, NIKL M, MAREŠ J A, et al. Luminescence and scintillation properties of YAG∶Ce single crystal and optical ceramics[J]. Journal of Luminescence, 2007, 126(1): 77-80.
[13] EULER F, BRUCE J A. Oxygen coordinates of compounds with garnet structure[J]. Acta Crystallographica, 1965, 19(6): 971-978.
[14] DOU R Q, ZHANG Q L, GAO J Y, et al. Rare-earth tantalates and niobates single crystals: promising scintillators and laser materials[J]. Crystals, 2018, 8(2): 55.
[15] LIU W J, SUN Z T, CHEN J Y, et al. Raman spectroscopy in colorectal cancer diagnostics: comparison of PCA-LDA and PLS-DA models[J]. Journal of Spectroscopy, 2016, 2016: 1-6.
[16] BACHMANN V, RONDA C, MEIJERINK A. Temperature quenching of yellow Ce³⁺ luminescence in YAG∶Ce[J]. Chemistry of Materials, 2009, 21(10): 2077-2084.
[17] 林莹,刘梦丽,庄乃锋.绿色荧光粉CaMoO₄∶Ho³⁺结构精修及光谱性质的研究.人工晶体学报,2020,49(9):1614-1619.
LIN Y, LIU M L, ZHUANG N F. Refinement and spectral properties of green phosphor CaMoO₄∶Ho³⁺. Journal of Synthetic Crystals, 2020, 49(9): 1614-1619(in Chinese).
[18] 方紫璇,于浩,钱小波,等.共掺调剂离子Na⁺/Gd³⁺调控Eu∶CaF₂晶体的发光特性研究.人工晶体学报,2020,49(8):1548-1554+1561.
FANG Z X, YU H, QIAN X B, et al. Luminescent properties of Eu∶CaF₂ crystal controlled by co-doping Na⁺/Gd³⁺. Journal of Synthetic Crystals, 2020, 49(8): 1548-1554+1561(in Chinese).
[19] STROBEL P, SCHMIECHEN S, SIEGERT M, et al. Narrow-band green emitting nitridolithoalumosilicate Ba[Li₂(Al₂Si₂)N₆]∶Eu²⁺ with framework topology whj for LED/LCD-backlighting applications[J]. Chemistry of Materials, 2015, 27(17): 6109-6115.
[20] CHI R, ZHOU Z, XU Z, et al. Solution-chemistry analysis of ammonium bicarbonate consumption in rare-earth-element precipitation[J]. Metallurgical and Materials Transactions B, 2003, 34(5): 611-617.
[21] DORENBOS P. The 5d level positions of the trivalent lanthanides in inorganic compounds[J]. Journal of Luminescence, 2000, 91(3/4): 155-176.
[22] TULEGENOVA A T, LISITSYN V M, LISITSYNA L A, et al. Luminescence of YAG∶Ce phosphors under excilamp irradiation[J]. Bulletin of the Russian Academy of Sciences: Physics, 2020, 84(7): 791-795.
[23] PAN Z F, LI W Q, XU Y, et al. Structure and redshift of Ce³⁺ emission in anisotropically expanded garnet phosphor MgY₂Al₄SiO₁₂∶Ce³⁺[J]. RSC Advances, 2016, 6(25): 20458-20466.

Luminescent Properties of LuGG∶Ce Nanophosphor Synthesized via Co-Precipitation Method

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	FENG Kai, LÜ Bin, CHENG Hongmei, WU Shaofan, WANG Yan, LIU Yongxing. Synthesis of Ultrafine TbO_1.81 and Tb₂O₃ Powders for Magneto-Optical Application [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2021, 50(1): 80-87.
[2]	PAN Rui, FU Min, CHEN Zhengbo, HU Xueli. Photocatalytic Degradation of Toluene by ZnSn(OH)₆/SrSn(OH)₆ [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2021, 50(1): 122-129.
[3]	RUAN Wenke, XIE Mubiao. Recent Research Progress on Tungsten and Molybdate Red Luminescent Material for White LED [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2021, 50(1): 167-178.
[4]	ZHANG Fang-yuan;XIE Jian-jun;WANG Tun;LIN De-bao;XIAO Wei-qin;SHI Ying;LEI Fang;ZHANG Lei. Synthesis and Luminescence Properties of Bi4Si3O12∶Sm3+ Phosphor [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2017, 46(8): 1493-1497.
[5]	CHEN Jie;ZHANG Qing;CHE Ming-chao. Preparation of Tetragonal Barium Titanate Nanopowders by Oxalate Co-precipitation Assisted with Microwave Method [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2017, 46(8): 1545-1551.
[6]	HAO Chen-hui;CUI Cai-e;HUANG Ping;WANG Lei;SHI Qiu-feng. Synthesis and Photoluminescence Properties of Red-emitting Phosphor SrSnO3∶Eu3+ [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2017, 46(6): 1009-1014.
[7]	LUO Jun-ming;JIAO Ya-mei;DENG Li-ping;XU Ji-lin. Preparation and Luminescent Properties of Y2O3∶Yb3+,Tm3+ Nanopowders [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2017, 46(3): 410-415.
[8]	CAI Shuai;LV Bin;WU Guan-jie;WANG Zhen-hai;CHEN Hong-bing. Preparation of Gd3 (In,Al) 5 O12∶Ce Garnet Powder by Co-precipitation Method [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2017, 46(1): 112-116.
[9]	BAI Gai-ling;TAN Jun-hua. Comparison of Two Preparation Methods and Methanol Electro-oxidation Properties of Nano NiCo2O4 [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2016, 45(7): 1970-1975.
[10]	ZHANG Rui-hao;DAI Jian-qing;LI Ya;CHENG Zhen-yu;WANG Zhi-xiang. Preparation and Properties of Multiferroic BiMn2O5 via Co-precipitation Method [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2016, 45(2): 529-534.
[11]	SUN Zhi;XIE Jian-jun;WANG Yu;SHI Ying;LEI Fang. Structure Evolution and Luminescent Properties of Tb∶Lu2SiO5 Optical Thin Films [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2016, 45(11): 2561-2566.
[12]	LIU Jia-nan;MA Wei-min;MA Lei;JI Lian-yong;WU Ying;WANG Hua-Lei. Preparation and Mechanical Properties of Gd2Ti2O7/ZrO2 (3Y) Ceramics [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2015, 44(4): 1077-1083.
[13]	LIU Hao-fei;DAI Jian-qing. Preparation of Single Phase BiFeO3 Powders by Co-precipitation Method and Physical Properties of Single Phase BiFeO3 Ceramics with High Density [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2015, 44(3): 692-698.
[14]	NIAN Hong-en;ZHOU Yuan;WU Zhi-jian;LI Xiang;SHEN Yue;ZENG Jin-bo. Study on Red Emission from Rare Earth Element Europium Doped Yttrium Borate Thin Films [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2015, 44(12): 3444-3448.
[15]	DONG Yuan-yuan;HUANG Rong;XU Jia-yue;ZHANG Yan. Synthesis and Luminescence Properties of NaY(Mo/WO4) 2:Eu3+ Phosphors [J]. JOURNAL OF SYNTHETIC CRYSTALS, 2015, 44(12): 3543-3547.