摘要/Abstract

摘要： 以处理后的脱硫石膏为原料,在H₂SO₄-H₂O体系中以Cu(NO₃)₂为晶形控制剂采用水热法制备脱硫石膏晶须,探讨了Cu(NO₃)₂对脱硫石膏晶须生长的影响机理。结果表明:Cu(NO₃)₂对脱硫石膏有明显促溶作用,其中Cu²⁺可减小溶液中各离子的活度系数,使溶液中的Ca²⁺浓度增大。NO^-₃通过静电作用在Ca²⁺周围聚集并对SO^2-₄产生屏蔽作用,导致脱硫石膏继续溶解并使Ca²⁺和SO^2-₄的浓度处于相对稳定状态,有利于半水脱硫石膏晶体的形核与生长。此外,Cu²⁺还可在晶须的生长过程中选择性吸附在晶须表面,生成CuSO₄,促进了脱硫石膏的结晶生长,最终在Cu(NO₃)₂用量为2.0%(质量分数)时制备的脱硫石膏晶须长径比约为73。

关键词: 脱硫石膏, 硝酸铜, 晶须, H₂SO₄-H₂O体系, 结晶, 影响机制

Abstract: Desulfurized gypsum whiskers were prepared by hydrothermal method using treated desulfurized gypsum as raw materials, and Cu(NO₃)₂ was used as the crystal form control agent in the H₂SO₄-H₂O system. The influence mechanism of Cu(NO₃)₂ on the growth of desulfurized gypsum whiskers was discussed. The results show that Cu(NO₃)₂ has obvious dissolution-promoting effect on desulfurized gypsum, and Cu²⁺ could reduce the activity coefficient of each ion in the solution and increase the concentration of Ca²⁺ in the solution. Moreover, NO^-₃ accumulate around Ca²⁺ and shield SO^2-₄ through electrostatic action, which cause the desulfurized gypsum dissolve continuously and keep the concentration of Ca²⁺ and SO^2-₄ in a relatively stable state, and facilitate the nucleation and growth of hemihydrate desulfurized gypsum crystals. In addition, Cu²⁺ selectively adsorb on the surface of the whiskers to generate CuSO₄ during the growth of the whiskers, thereby improve the crystal growth of desulfurized gypsum whiskers. When the amount of Cu(NO₃)₂ is 2.0% (mass fraction), desulfurized gypsum whiskers with an aspect ratio of about 73 are prepared.

Key words: desulfurized gypsum, Cu(NO₃)₂, whisker, H₂SO₄-H₂O system, crystallization, influence mechanism

中图分类号:

TQ177.3
O784

汪潇, 马晓晓, 金彪, 张小婷, 张建武, 杨留栓, 王宇斌. H₂SO₄-H₂O中硝酸铜对脱硫石膏晶须生长的影响[J]. 人工晶体学报, 2021, 50(12): 2316-2322.

WANG Xiao, MA Xiaoxiao, JIN Biao, ZHANG Xiaoting, ZHANG Jianwu, YANG Liushuan, WANG Yubin. Influence of Cu(NO₃)₂ in H₂SO₄-H₂O on the Growth of Desulfurized Gypsum Whiskers[J]. JOURNAL OF SYNTHETIC CRYSTALS, 2021, 50(12): 2316-2322.

参考文献

[1] 李强,刘福立,尚超,等.微波外场强化电石渣制备硫酸钙晶须及其机理分析[J].人工晶体学报,2020,49(1):125-130.
LI Q, LIU F L, SHANG C, et al. Preparation of calcium sulfate whiskers by microwave-enhanced carbide slag and its mechanism analysis[J]. Journal of Synthetic Crystals, 2020, 49(1): 125-130(in Chinese).
[2] LIU C J, ZHAO Q, WANG Y G, et al. Surface modification of calcium sulfate whisker prepared from flue gas desulfurization gypsum[J]. Applied Surface Science, 2016, 360: 263-269.
[3] FENG X, ZHANG Y, WANG G L, et al. Dual-surface modification of calcium sulfate whisker with sodium hexametaphosphate/silica and use as new water-resistant reinforcing fillers in papermaking[J]. Powder Technology, 2015, 271: 1-6.
[4] 李强,刘福立,尚超,等.脱硫石膏制备硫酸钙晶须结晶动力学研究[J].人工晶体学报,2018,47(11):2305-2310.
LI Q, LIU F L, SHANG C, et al. Study on crystallization kinetics of calcium sulfate whisker prepared by desulfurization gypsum[J]. Journal of Synthetic Crystals, 2018, 47(11): 2305-2310(in Chinese).
[5] WANG X, JIN B, YANG L S, et al. Effect of CuCl₂on hydrothermal crystallization of calcium sulfate whiskers prepared from FGD gypsum[J]. Crystal Research and Technology, 2015, 50(8): 633-640.
[6] 马文静,陈学青,郜丽丽,等.脱硫石膏制备γ-CaSO₄晶须及Ⅱ-CaSO₄晶须[J].高校化学工程学报,2021,35(3):520-528.
MA W J, CHEN X Q, GAO L L, et al. Preparation of γ-CaSO₄ and Ⅱ-CaSO₄ whiskers using FGD gypsum[J]. Journal of Chemical Engineering of Chinese Universities, 2021, 35(3): 520-528(in Chinese).
[7] 唐明亮,沈晓冬,黄金龙.晶习改变剂对α-CaSO₄·0.5H₂O晶体形貌的作用机理[J].建筑材料学报,2014,17(2):280-283+308.
TANG M L, SHEN X D, HUANG J L. Mechanism of crystal growth habit modifiers on the morphology of α-CaSO₄·0.5H₂O crystal[J]. Journal of Building Materials, 2014, 17(2): 280-283+308(in Chinese).
[8] 张巨松,郑万荣,陈华,等.影响α半水石膏粒度、形貌及强度的因素[J].沈阳建筑大学学报(自然科学版),2006,22(6):930-934.
ZHANG J S, ZHENG W R, CHEN H, et al. Research of some actors on influencing the granularity, morphology and strength of alpha-hemihydrate gypsum[J]. Journal of Shenyang Jianzhu University (Natural Science), 2006, 22(6): 930-934(in Chinese).
[9] 方羊.水热法制备半水硫酸钙晶须及其长径比的可控研究[D].合肥:合肥工业大学,2017.
FANG Y. Calcium sulfate hemihydrate whiskers prepared by hydrothermal method and the controllability study of aspect ratios[D]. Hefei: Hefei University of Technology, 2017(in Chinese).
[10] 陈平,田宇,胡成.盐溶液种类和浓度对α-半水脱硫石膏合成的影响[J].无机盐工业,2020,52(10):130-134.
CHEN P, TIAN Y, HU C. Effect of type and concentration of salt solution on synthesis of α-semi-water desulfurization gypsum[J]. Inorganic Chemicals Industry, 2020, 52(10): 130-134(in Chinese).
[11] GUAN Q J, SUN W, HU Y H, et al. A facile method of transforming FGD gypsum to α-CaSO₄·0.5H₂O whiskers with cetyltrimethylammonium bromide (CTAB) and KCl in glycerol-water solution[J]. Scientific Reports, 2017, 7: 7085.
[12] 汪潇,杨留栓,朱新峰,等.K₂SO₄/KCl添加剂对脱硫石膏晶须结晶的影响[J].人工晶体学报,2013,42(12):2661-2668.
WANG X, YANG L S, ZHU X F, et al. Effect of K₂SO₄/KCl additive on the crystallization of desulfurization gypsum whisker[J]. Journal of Synthetic Crystals, 2013, 42(12): 2661-2668(in Chinese).
[13] 李强,尚超,石棕文,等.金属离子对硫酸钙晶须形貌影响的试验研究[J].非金属矿,2019,42(1):94-96.
LI Q, SHANG C, SHI Z W, et al. Experimental study on the effect of metal ions on the morphology of calcium sulfate whiskers[J]. Non-Metallic Mines, 2019, 42(1): 94-96(in Chinese).
[14] RABIZADEH T, STAWSKI T M, MORGAN D J, et al. The effects of inorganic additives on the nucleation and growth kinetics of calcium sulfate dihydrate crystals[J]. Crystal Growth & Design, 2017, 17(2): 582-589.
[15] ZHANG X T, WANG X, JIN B, et al. Crystal structure formation of hemihydrate calcium sulfate whiskers (HH-CSWs) prepared using FGD gypsum[J]. Polyhedron, 2019, 173: 114140.
[16] 汪潇,金彪,张小婷,等.MgSO₄/MgCl₂对脱硫石膏溶解度及其晶须结晶的影响[J].河南科技大学学报(自然科学版),2018,39(2):6-10+24+4.
WANG X, JIN B, ZHANG X T, et al. Effects of MgSO₄/MgCl₂ on FGD gypsum solubility and whisker crystallization[J]. Journal of Henan University of Science and Technology (Natural Science), 2018, 39(2): 6-10+24+4(in Chinese).
[17] ZHENG X X, JING H J, FENG J Q, et al. Study on the solubility and morphology of calcium sulfate dihydrate in nitric acid and phosphoric acid aqueous medium[C]//2010 International Conference on Mechanic Automation and Control Engineering. June 26-28, 2010, Wuhan, China. IEEE, 2010: 3931-3934.
[18] 徐春华,李英峰,胡松青.硝酸钾电解质溶液的结构和热力学性质的计算机分子模拟[J].中国石油大学学报(自然科学版),2006,30(2):101-105+132.
XU C H, LI Y F, HU S Q. A computer simulation study on structure and thermodynamic property of KNO₃ electrolyte solution[J]. Journal of China University of Petroleum (Edition of Natural Science), 2006, 30(2): 101-105+132(in Chinese).
[19] 汪潇,金彪,王宇斌,等.阴离子在脱硫石膏晶须水热结晶中的作用机理[J].高等学校化学学报,2020,41(3):473-480.
WANG X, JIN B, WANG Y B, et al. Interaction mechanism of anions in hydrothermal crystallization of desulfurization gypsum whiskers[J]. Chemical Journal of Chinese Universities, 2020, 41(3): 473-480(in Chinese).
[20] YANG L S, WANG X, ZHU X F, et al. Preparation of calcium sulfate whisker by hydrothermal method from flue gas desulfurization (FGD) gypsum[J]. Applied Mechanics and Materials, 2012, 268/269/270: 823-826.
[21] FELDMANN T, DEMOPOULOS G P. Influence of impurities on crystallization kinetics of calcium sulfate dihydrate and hemihydrate in strong HCl-CaCl₂ solutions[J]. Industrial & Engineering Chemistry Research, 2013, 52(19): 6540-6549.
[22] DONG F Q, HUANG Z Y, TAN H B, et al. Effect of additives on calcium sulfate hemihydrate whiskers morphology from calcium sulfate dehydrate and phosphogypsum[J]. Materials and Manufacturing Processes, 2016, 31(15): 2037-2043.

H₂SO₄-H₂O中硝酸铜对脱硫石膏晶须生长的影响

Influence of Cu(NO₃)₂ in H₂SO₄-H₂O on the Growth of Desulfurized Gypsum Whiskers

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	陈星辉, 唐颖慧, 王加强, 柴晗阳, 魏新琪, 陈光伟. 衬底温度对氧化锌薄膜微结构及光学性能的影响[J]. 人工晶体学报, 2021, 50(9): 1681-1687.
[2]	姬凯迪, 高灿灿, 杨发顺, 熊倩, 马奎. 后退火气氛对磁控溅射制备β-Ga₂O₃薄膜材料的影响[J]. 人工晶体学报, 2021, 50(6): 1056-1061.
[3]	于亚杰, 郑强, 刘海利, 邢润, 李雪. 方解石制备碳酸钙晶须的影响因素及机理[J]. 人工晶体学报, 2021, 50(6): 1112-1122.
[4]	綦正超, 许庭翔, 刘学超, 王丁. 杂质和缺陷对SiC单晶导热性能的影响[J]. 人工晶体学报, 2021, 50(5): 816-824.
[5]	王东意, 郑强, 于亚杰, 徐少伟, 王禹博, 邓晓阳, 曹笑宁, 岳岩, 李雪, 刘云义. 白云石精制液中不同离子对碳酸钙晶须的影响[J]. 人工晶体学报, 2021, 50(5): 908-914.
[6]	邱武, 刘向阳. 以晶体生长原理重塑蚕丝柔性材料世界的未来[J]. 人工晶体学报, 2021, 50(4): 629-647.
[7]	宋舒虹, 姚昌林, 王蕾, 曲亚倩, 陶绪堂. 药物结晶中的经典与非经典结晶路径[J]. 人工晶体学报, 2021, 50(4): 669-684.
[8]	张晓勇, 张琰春, 张晓玉, 张森. 化学水浴沉积法制备硫化镉薄膜的微结构和性能[J]. 人工晶体学报, 2021, 50(2): 310-317.
[9]	叶文君, 陈玉梅, 陈冬梅, 郭倩, 周志旭. 5-溴-2-(4-甲基哌啶-1-基)嘧啶的晶体结构及密度泛函理论研究[J]. 人工晶体学报, 2021, 50(11): 2116-2122.
[10]	卢鹏;胡雪利;潘睿;陈正波. CaCO3/g-C3N4复合材料的制备及吸附性能研究[J]. 人工晶体学报, 2020, 49(9): 1691-1698.
[11]	范天博;韩冬雪;贾晓辉;陈思;姜宇;胡婷婷;郭洪范;李莉;刘云义. NH4+-NH3缓冲体系制备碱式硫酸镁晶须及生长机理[J]. 人工晶体学报, 2020, 49(9): 1721-1727.
[12]	李宝珠;高彦昭;王健;程红娟;陈毅;姚宝权. 高质量CdSe单晶生长及其OPO性能研究[J]. 人工晶体学报, 2020, 49(8): 1517-1522.
[13]	刘欢;朱如忠;龚建超;王琦琨;付丹扬;雷丹;黄嘉丽;吴亮. 高温退火工艺对直流反应磁控溅射制备蓝宝石基氮化铝模板的影响[J]. 人工晶体学报, 2020, 49(8): 1541-1547.
[14]	邓海山;姚舜;周月霞;陈甲;曹敏驰;王友法. 小尺寸、单分散Cd2+掺杂β-NaLuF∶Yb,Er上转换纳米晶的合成[J]. 人工晶体学报, 2020, 49(7): 1208-1216.
[15]	张浩然;陈帅峰;陈庆;骆丽杰;李建保;陈拥军. 熔盐辅助碳热还原氮化法制备氮化钽晶须[J]. 人工晶体学报, 2020, 49(7): 1294-1299.