不同形貌TiO2薄膜的可控制备及其光电化学性能研究

摘要/Abstract

摘要： 采用水热法在FTO(fluorine-doped tin oxide)基底上制备不同形貌的锐钛矿结构TiO₂薄膜。通过不断增大反应前驱物中盐酸浓度,TiO₂薄膜由球状颗粒薄膜逐渐演变生长成大面积高能(001)面裸露的TiO₂纳米片阵列薄膜。通过对形貌演化规律及X射线衍射图谱变化规律进行分析,提出了不同形貌TiO₂薄膜的生长演化机制,并对盐酸在其中的作用进行了说明。为了进一步改善TiO₂薄膜的性能,采用连续离子层吸附反应法对不同形貌的TiO₂薄膜进行CdS量子点敏化。采用紫外可见吸收光谱分析法和三电极体系对复合薄膜的光吸收性能和光电化学(PEC)性能进行了研究,实验数据显示CdS/TiO₂复合薄膜的光电化学性能皆明显优于单纯TiO₂薄膜,而且纳米片阵列薄膜的性能明显优于其他形貌薄膜,说明了大面积高能(001)面裸露的TiO₂纳米片阵列薄膜的性能优越性。

关键词: TiO₂薄膜, (001)晶面, 晶体生长, 水热法, 量子点, 敏化

Abstract: Anatase TiO₂ thin films with different morphology were prepared on FTO substrates by hydrothermal method. With the increasing of hydrochloric acid concentration in the precursor, TiO₂ thin films gradually evolved from spherical particle films into TiO₂ nanosheet array films with a large percentage of high-energy exposed (001) planes. By analyzing the evolution rule of morphology and X-ray diffraction patterns, a reasonable growth and evolution mechanism of TiO₂ thin film with different morphology was proposed, and the role of hydrochloric acid was explained. In order to further improve the performance of TiO₂ thin films, CdS quantum dots (QDs) sensitization was performed on different TiO₂ thin films by the successive ionic layer adsorption and reaction method. The optical absorption performance and photoelectrochemical (PEC) properties of composite films were studied by ultraviolet visible absorption spectroscopy and three-electrode electrochemistry system. The optical absorption data and PEC performance data show that the properties of CdS/TiO₂ composite films are better than those of pure TiO₂ thin films, and the properties of nanosheet array films are obviously better than other morphologies, which illustrates the performance superiority of TiO₂ nanosheet array films with large area high-energy (001) planes exposed. The excellent PEC properties also suggest that the QDs sensitized TiO₂ nanosheet array films with a large percentage of high-energy surfaces have potential applications in PEC solar cells.

Key words: TiO₂ thin film, (001) lattice plane, crystal growth, hydrothermal method, quantum dot, sensitization

中图分类号:

王鑫伟, 车致远, 张兴, 李玲薇, 张伟, 苏适, 马晋文. 不同形貌TiO₂薄膜的可控制备及其光电化学性能研究[J]. 人工晶体学报, 2021, 50(3): 516-522.

WANG Xinwei, CHE Zhiyuan, ZHANG Xing, LI Lingwei, ZHANG Wei, SU Shi, MA Jinwen. Controllable Preparation and Photoelectrochemical Performance of TiO₂ Thin Film with Different Morphology[J]. Journal of Synthetic Crystals, 2021, 50(3): 516-522.

参考文献

[1] FUJISHIMA A, HONDA K.Electrochemical photolysis of water at a semiconductorelectrode[J]. Nature, 1972, 238(5358): 37-38.
[2] GRÄTZEL M. Photoelectrochemical cells[J]. Nature, 2001, 414(6861): 338-344.
[3] CHO I S, LEE C H, FENG Y, et al.Codoping titanium dioxide nanowires with tungsten and carbon for enhanced photoelectrochemical performance[J]. Nature Communications, 2013, 4: 1723.
[4] BACH U, LUPO D, COMTE P, et al.Solid-state dye-sensitizedmesoporous TiO₂ solar cells with high photon-to-electron conversion efficiencies[J]. Nature, 1998, 395(6702): 583-585.
[5] GRÄTZEL M. Molecular photovoltaics that mimic photosynthesis[J]. Pure and Applied Chemistry, 2001, 73(3): 459-467.
[6] HAGFELDT A, BOSCHLOO G, SUN L C, et al.Dye-sensitized solar cells[J]. Chemical Reviews, 2010, 110(11): 6595-6663.
[7] YELLA A, LEE H W, TSAO H N, et al.Porphyrin-sensitized solar cells with cobalt (II/III)-based redox electrolyte exceed 12 percent efficiency[J]. Science, 2011, 334(6056): 629-634.
[8] CROSSLAND E J W, NOEL N, SIVARAM V, et al. Mesoporous TiO₂ single crystals delivering enhanced mobility and optoelectronic device performance[J]. Nature, 2013, 495(7440): 215-219.
[9] CHUNG I, LEE B, HE J Q, et al.All-solid-state dye-sensitized solar cells with high efficiency[J]. Nature, 2012, 485(7399): 486-489.
[10] WANG Z S, KAWAUCHI H, KASHIMA T, et al.Significant influence of TiO₂ photoelectrode morphology on the energy conversion efficiency of N719 dye-sensitized solar cell[J]. Coordination Chemistry Reviews, 2004, 248(13/14): 1381-1389.
[11] LIU G, YANG H G, PAN J, et al.Titanium dioxide crystals with tailored facets[J]. Chemical Reviews, 2014, 114(19): 9559-9612.
[12] OHNO T,SARUKAWA K, MATSUMURA M.Crystal faces of rutile and anatase TiO₂ particles and their roles in photocatalytic reactions[J]. New Journal of Chemistry, 2002, 26(9): 1167-1170.
[13] ANPO M, TAKEUCHI M.The design and development of highly reactive titanium oxidephotocatalysts operating under visible light irradiation[J]. Journal of Catalysis, 2003, 216(1/2): 505-516.
[14] ZHANG J, XU Q, FENG Z C, et al.Importance of the relationship between surface phases and photocatalytic activity of TiO₂[J]. Angewandte Chemie, 2008, 120(9): 1790-1793.
[15] YANG H G, SUN C H, QIAO S Z, et al.Anatase TiO₂ single crystals with a large percentage of reactive facets[J]. Nature, 2008, 453(7195): 638-641.
[16] LI T Y, TIAN B Z, ZHANG J L, et al.Facile tailoring of anatase TiO₂ morphology by use of H₂O₂: from microflowers with dominant {101} facets to microspheres with exposed {001} facets[J]. Industrial & Engineering Chemistry Research, 2013, 52(20): 6704-6712.
[17] WANG H E, CHEN Z H, LEUNG Y H, et al.Hydrothermal synthesis of ordered single-crystalline rutile TiO₂ nanorod arrays on different substrates[J]. Applied Physics Letters, 2010, 96(26): 263104.
[18] PAN J, WU X, WANG L, et al.Synthesis of anatase TiO₂ rods with dominant reactive {010} facets for the photoreduction of CO₂ to CH₄ and use in dye-sensitized solar cells[J]. Chemical Communications (Cambridge, England), 2011, 47(29): 8361-8363.
[19] LAZZERI M, VITTADINI A, SELLONI A.Structure and energetics of stoichiometric TiO₂ anatase surfaces[J]. Physical Review B, 2001, 63(15): 155409.
[20] ZHANG Q H, GAO L, GUO J K.Effects of calcination on the photocatalytic properties of nanosized TiO₂ powders prepared by TiCl₄ hydrolysis[J]. Applied Catalysis B: Environmental, 2000, 26(3): 207-215.
[21] YANG X H, LI Z, LIU G, et al.Ultra-thinanatase TiO₂nanosheets dominated with {001} facets: thickness-controlled synthesis, growth mechanism and water-splitting properties[J]. Cryst Eng Comm, 2011, 13(5): 1378-1383.

不同形貌TiO₂薄膜的可控制备及其光电化学性能研究

Controllable Preparation and Photoelectrochemical Performance of TiO₂ Thin Film with Different Morphology

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	许万里, 甘云海, 李悦文, 李彬, 郑有炓, 张荣, 修向前. 高均匀性6英寸GaN厚膜的高速率HVPE生长研究[J]. 人工晶体学报, 2025, 54(1): 11-16.
[2]	程友良, 杜慧彬, 张忠宝, 王凯. 二氧化锡基染料敏化太阳能电池电子传输模型优化及器件性能研究[J]. 人工晶体学报, 2024, 53(9): 1629-1639.
[3]	孙元龙, 胡子钰, 郑国宗. 大尺寸CH₃NH₃PbBr₃晶体生长和光电性能表征[J]. 人工晶体学报, 2024, 53(8): 1313-1318.
[4]	马启司, 刘江高, 折伟林, 曹聪, 张立超, 赵超, 范叶霞, 周振奇. 基于CGSim模拟的炉膛空气对流对碲锌镉晶体生长温场影响研究[J]. 人工晶体学报, 2024, 53(8): 1344-1351.
[5]	陈继虎, 路亚妮. 粉体还原对硒化亚铜热电性能的影响[J]. 人工晶体学报, 2024, 53(8): 1464-1470.
[6]	凌昊, 徐乐, 陈思贤, 唐远之, 孙海滨, 郭学, 冯玉润, 胡强强. 溶液法生长大尺寸CsCu₂I₃钙钛矿单晶及其光学性能研究[J]. 人工晶体学报, 2024, 53(7): 1121-1126.
[7]	伍仕停, 余春燕, 方佳庆, 徐阳, 翟光美. ZnSe基蓝光量子点的中间壳层结构调控及其发光性能研究[J]. 人工晶体学报, 2024, 53(7): 1160-1169.
[8]	艾家辛, 万洪平, 钱俊兵, 韦华. VGF法磷化铟单晶炉加热器对炉内热场分布影响的研究[J]. 人工晶体学报, 2024, 53(5): 781-791.
[9]	蔡小勇, 姜洪喜. 红色荧光粉CaWO₄∶Eu³⁺,Bi³⁺的制备和光学性能的研究[J]. 人工晶体学报, 2024, 53(5): 833-840.
[10]	邢佳斌, 李威, 贾松岩, 马亚丽, 李雪, 郑强. 低温碳化法制备高分散性纳米碳酸钙的研究[J]. 人工晶体学报, 2024, 53(5): 864-872.
[11]	黄昌保, 胡倩倩, 朱志成, 李亚, 毛长宇, 徐俊杰, 吴海信, 倪友保. 中长波Cr²⁺/Fe²⁺∶CdSe激光晶体生长及元件制备[J]. 人工晶体学报, 2024, 53(4): 551-553.
[12]	秦峰, 吴金杰, 邓宁勤, 焦志伟, 朱伟峰, 汤显强, 赵瑞. 基于溶液法制备卤化铅钙钛矿的直接型辐射探测器研究进展[J]. 人工晶体学报, 2024, 53(4): 554-571.
[13]	曹聪, 刘江高, 范叶霞, 李振兴, 周振奇, 马启司, 牛佳佳. 碲锌镉晶体生长温度梯度与界面形状稳定性关系的研究[J]. 人工晶体学报, 2024, 53(4): 641-648.
[14]	康杰, 丁紫阳, 王晓燕, 李连荣, 孙为云, 焦璨, 宋月鹏. 腐蚀法制备SiC量子点粒径调控及尺寸对其光学性能的影响[J]. 人工晶体学报, 2024, 53(4): 684-691.
[15]	李波, 王霏宇, 沈红, 毛逢银, 李勇辉. 基于4-羟基间苯二甲酸和含氮杂环配体的Zn(II)配合物的合成、晶体结构与荧光性质研究[J]. 人工晶体学报, 2024, 53(4): 692-700.