高性能刷状ZnO介晶的制备及其对复合树脂性能的增强作用

摘要/Abstract

摘要： 无机填料作为齿科复合树脂的主要成分,对其性能影响最为显著。本文以阿拉伯胶为结构导向剂,用热水解法合成了多孔、分级结构的刷状ZnO介晶,其厚度和直径分别为1.2 μm和1.0 μm。通过微流控制法在其表面包覆了4~6 nm无定形SiO₂,以利于其表面硅烷化。通过场发射扫描电镜(FE-SEM)、X射线衍射仪(XRD)、热重分析仪(TGA)等对其进行了表征。对ZnO@SiO₂进行硅烷改性处理后,将其作为辅助填料,与改性纳米SiO₂主填料一起添加到Bis-GMA/TEGDMA树脂体系中,光固化得到齿科复合树脂。力学测试表明,ZnO@SiO₂填充质量分数控制在5%以内时可有效提高复合树脂力学性能。与单一二氧化硅填料的复合树脂相比,添加填充质量分数3% ZnO@SiO₂,复合树脂的力学性能表现最佳,其弯曲强度、弯曲模量和压缩强度分别提高了12.9%、6.6%和3.7%,同时还表现出优良的抗菌活性,对变异链球菌抗菌率达98.7%。此外,添加了ZnO@SiO₂介晶填料的复合树脂还具备更好的耐磨性。

关键词: 齿科树脂, 氧化锌介晶, 力学性能, 抗菌性能

Abstract: The inorganic filler is the main component of dental resin composite, which is very important for the properties of resin composite. In this paper, ZnO mesocrystals with porous and hierarchical structure were achieved by a thermal hydrolysis method using gum arabic as structure-directing agent. The thickness and diameter of the synthesized ZnO mesocrystals were about 1.2 μm and 1.0 μm. The amorphous silica in a thickness of 4~6 nm was uniformly coated on the surface of ZnO mesocrystals via the microfluidc process. ZnO mesocrystals were characterized by field-emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD) and thermogravimetric analysis (TGA). The ZnO@SiO₂ was firstly modified with 3-methacryloxypropyl trimethoxysilane (γ-MPS), and mixed with modified SiO₂ nanoparticles as co-filler. Subsequently modified inorganic particles were added into Bis-GMA/TEGDMA to prepare dental composite resin by light-curing. The mechanical testing show that the mass fraction of ZnO@SiO₂ (≤5%) could improve the mechanical properties of composite resin effectively. The silica matrix composite resin filled with 3% ZnO@SiO₂ demonstrates the best mechanical properties, among which the flexural strength, flexural modulus and compression strength increase by 12.9%, 6.6% and 3.7%, respectively, in comparison with the composite using of only SiO₂ filler. This optimal composite also exhibits superior antimicrobial activity, with antibacterial rate up to 98.7% to Streptococcus mutans. In addition, the composite resin with ZnO@SiO₂ also has better wear resistance.

Key words: dental resin, ZnO mesocrystal, mechanical property, antibacterial property

中图分类号:

TB332

秦阳, 张青红, 王瑞莉, 刘梅. 高性能刷状ZnO介晶的制备及其对复合树脂性能的增强作用[J]. 人工晶体学报, 2021, 50(3): 548-557.

QIN Yang, ZHANG Qinghong, WANG Ruili, LIU Mei. Preparation of High Performance Brush-Like Zinc Oxide Mesocrystals and Its Reinforcing Effect on Properties of Resin Composites[J]. Journal of Synthetic Crystals, 2021, 50(3): 548-557.

参考文献

[1] PETERSEN P E, BOURGEOIS D, OGAWA H, et al.Theglobal burden of oral diseases and risks to oral health[J]. Bulletin of the World Health Organization, 2005, 83(9): 661-669.
[2] MUSANJE L, FERRACANE J L, FERRACANE L L.Effects of resin formulation and nanofiller surface treatment on in vitro wear of experimental hybrid resin composite[J]. Journal of Biomedical Materials Research Part B: Applied Biomaterials, 2006, 77B(1): 120-125.
[3] KARABELA M M, SIDERIDOU I D.Synthesis and study of properties of dental resin composites with different nanosilica particles size[J]. Dental Materials, 2011, 27(8): 825-835.
[4] DEMARCO F F, CORRÊA M B, CENCI M S, et al. Longevity of posterior composite restorations: not only a matter of materials[J]. Dental Materials, 2012, 28(1): 87-101.
[5] MOSZNER N, HIRT T.New polymer-chemical developments in clinical dental polymer materials:enamel-dentin adhesives and restorative composites[J]. Journal of Polymer Science Part A: Polymer Chemistry, 2012, 50(21): 4369-4402.
[6] NIU L N, FANG M, JIAO K, et al.Tetrapod-like zinc oxide whisker enhancement of resin composite[J]. Journal of Dental Research, 2010, 89(7): 746-750.
[7] KIM J W, KIM L U, KIM C K.Size control of silica nanoparticles and their surface treatment for fabrication of dental nanocomposites[J]. Biomacromolecules, 2007, 8(1): 215-222.
[8] FINLAY N, HAHNEL S, DOWLING A H, et al.The in vitro wear behavior of experimental resin-based composites derived from a commercial formulation[J]. Dental Materials, 2013, 29(4): 365-374.
[9] MITRA S B, WU D, HOLMES B N.An application of nanotechnology in advanced dental materials[J]. The Journal of the American Dental Association, 2003, 134(10): 1382-1390.
[10] Sturm E V, Cölfen H.Mesocrystals: past, presence, future[J]. Crystals, 2017, 7(7): 207.
[11] FLOQUET N, VIELZEUF D.Ordered misorientations and preferential directions of growth inmesocrystalline red coral sclerites[J]. Crystal Growth & Design, 2012, 12(10): 4805-4820.
[12] 杨士林,宋微.PASP调控球形碳酸钙沉积过程研究[J].人工晶体学报,2013,42(7):1475-1480.
YANG S L, SONG W.Study on precipitation process of spherical calcium carbonate controlled bypolyaspartic acid[J]. Journal of Synthetic Crystals, 2013, 42(7): 1475-1480(in Chinese).
[13] 张克从. 晶体结构与性能关系及其发展[J].人工晶体,1985,14(Z1):11.
ZHANG K C.Crystal structure—property relations and its developments[J]. Journal of Synthetic Crystals, 1985, 14(Z1): 11(in Chinese).
[14] TANG H, CHANG J C, SHAN Y Y, et al.Surfactant-assisted alignment of ZnO nanocrystals to superstructures[J]. The Journal of Physical Chemistry B, 2008, 112(13): 4016-4021.
[15] 刘玉玲,王瑞莉,李楠,等.ZnO介晶填料的制备及其齿科复合树脂的性能[J].无机材料学报,2019,34(10):1077-1084.
LIU Y L, WANG R L, LI N, et al.Preparation of zinc oxidemesocrystal filler and its properties as dental composite resin[J]. Journal of Inorganic Materials, 2019, 34(10): 1077-1084(in Chinese).
[16] NATALIO F, CORRALES T P,PANTHÖFER M, et al. Flexible minerals: self-assembled calcite spicules with extreme bending strength[J]. Science, 2013, 339(6125): 1298-1302.
[17] CHENG L, WEIR M D, ZHANG K, et al.Antibacterial nanocomposite with calcium phosphate and quaternary ammonium[J]. Journal of Dental Research, 2012, 91(5): 460-466.
[18] PENG J J Y, BOTELHO M G, MATINLINNA J P. Silver compounds used in dentistry for caries management: a review[J]. Journal of Dentistry, 2012, 40(7): 531-541.
[19] AYDIN SEVINÇ B, HANLEY L.Antibacterial activity of dental composites containing zinc oxide nanoparticles[J]. Journal of Biomedical Materials Research Part B: Applied Biomaterials, 2010, 94B(1): 22-31.
[20] LIU M H, TSENG Y H, GREER H F, et al.Dipole field guided orientated attachment ofnanocrystals to twin-brush ZnO mesocrystals[J]. Chemistry-A European Journal, 2012, 18(50): 16104-16113.
[21] MIAO X L, LI Y G,ZHANG Q H, et al.Low shrinkage light curable dental nanocomposites using SiO₂ microspheres as fillers[J]. Materials Science and Engineering: C, 2012, 32(7): 2115-2121.
[22] KESHMIRI M, KESLER O.Colloidal formation of monodisperse YSZ spheres: kinetics of nucleation and growth[J].Acta Materialia, 2006, 54(16): 4149-4157.
[23] WEI Y, LIU S J, XIAO Z H, et al.Enamel repair with amorphous ceramics[J]. Advanced Materials, 2020, 32(7): 1907067.
[24] KRAFT D J, VLUG W S,VAN KATS C M, et al. Self-assembly of colloids with liquid protrusions[J]. Journal of the American Chemical Society, 2009, 131(3): 1182-1186.
[25] GREER H F, ZHOU W Z, LIU M H, et al.The origin of ZnO twin crystals in bio-inspired synthesis[J]. Cryst Eng Comm, 2012, 14(4): 1247-1255.
[26] TSENG Y H, LIN H Y, LIU M H, et al.Biomimetic synthesis of nacrelike faceted mesocrystals of ZnO-Gelatin composite[J]. The Journal of Physical Chemistry C, 2009, 113(42): 18053-18061.
[27] FERREIRA C S, SANTOS P L, BONACIN J A, et al.Rice husk reuse in the preparation of SnO₂/SiO₂ Nanocomposite[J]. Materials Research, 2015, 18(3): 639-643.
[28] CHEN T M, BRAUER G M.Solvent effects on bonding organo-silane to silica surfaces[J]. Journal of Dental Research, 1982, 61(12): 1439-1443.
[29] WANG R L, BAO S, LIU F W, et al.Wear behavior of light-cured resin composites with bimodal silica nanostructures as fillers[J]. Materials Science and Engineering: C, 2013, 33(8): 4759-4766.
[30] YOSHIDA K, TANAGAWA M, ATSUTA M.Effects of filler composition and surface treatment on the characteristics of opaque resin composites[J]. Journal of Biomedical Materials Research, 2001, 58(5): 525-530.
[31] JIN J F, WEI G Y, HAO A L, et al.ZnO-AlBw-reinforced dental resin composites: the effect of pH level on mechanical properties[J]. RSC Advances, 2015, 5(33): 26430-26437.
[32] YAHYAZADEHFAR M, AROLA D.The role of organic proteins on the crack growth resistance of human enamel[J].Acta Biomaterialia, 2015, 19: 33-45.
[33] BAJAJ D, PARK S, QUINN G D, et al.Fracture processes and mechanisms of crack growth resistance in human enamel[J].JOM, 2010, 62(7): 76-82.
[34] LIU Y, TAN Y N, LEI T, et al.Effect of porous glass-ceramic fillers on mechanical properties of light-cured dental resin composites[J]. Dental Materials, 2009, 25(6): 709-715.
[35] 谢周杰,张昭,刘力伟,等.变形链球菌中的次级代谢产物及其在口腔生物被膜中的生态功能[J].生物工程学报,2017,33(9): 1547-1554.
XIE Z, ZHANG Z, LIU L, et al.Secondary metabolites from Streptococcusmutans and their ecological roles in dental biofilm[J]. Chinese Journal of Biotechnology, 2017, 33(9): 1547-1554.
[36] LEMOS J A, PALMER S R, ZENG L, et al.The biology of streptococcusmutans[J]. Microbiology Spectrum, 2019, 7(1).DOI:10.1128/microbiolspec.gpp3-0051-2018.
[37] TAM K H, DJURIŠI<inline-formula><mml:math xmlns:mml="http://www.w3.org/1998/Math/MathML" id="Mml1-1000-985X-35-3-548"><mml:mover><mml:mrow><mml:mi mathvariant="normal">C</mml:mi></mml:mrow><mml:mrow><mml:mi>'</mml:mi></mml:mrow></mml:mover></mml:math></inline-formula> A B, CHAN C M N, et al. Antibacterial activity of ZnO nanorods prepared by a hydrothermal method[J]. Thin Solid Films, 2008, 516(18): 6167-6174.
[38] GHAZAL M, YANG B,LUDWIG K, et al.Two-body wear of resin and ceramic denture teeth in comparison to human enamel[J]. Dental Materials, 2008, 24(4): 502-507.
[39] TURSSI C P, DE MORAES PURQUERIO B, SERRA M C. Wear of dental resin composites: insights into underlying processes and assessment methods—a review[J]. Journal of Biomedical Materials Research Part B: Applied Biomaterials, 2003, 65B(2): 280-285.
[40] XING X S, LI R K Y. Wear behavior of epoxy matrix composites filled with uniform sized sub-micron spherical silica particles[J]. Wear, 2004, 256(1/2): 21-26.
[41] YESIL Z D, ALAPATI S, JOHNSTON W, et al.Evaluation of the wear resistance of new nanocomposite resinrestorative materials[J]. The Journal of Prosthetic Dentistry, 2008, 99(6): 435-443.