基于单体石墨纤维的场发射特性研究

人工晶体学报 ›› 2021, Vol. 50 ›› Issue (5): 866-870.

基于单体石墨纤维的场发射特性研究

霍海波, 郑亚娟, 麻华丽, 董子华, 李倩倩, 李明玉, 丁佩, 曾凡光

郑州航空工业管理学院材料学院,郑州 450015

收稿日期:2021-03-08 出版日期:2021-05-15 发布日期:2021-06-15
通讯作者: 曾凡光,博士,教授。E-mail:fgzeng@sina.com
作者简介:霍海波(1980—),男,河北省人,副教授。E-mail:hhb-18@163.com
基金资助:
河南省科技厅科技攻关项目(202102210110,202102210246);河南省自然科学基金(212300410414);航空科学基金(2019ZF055002)

Field Emission Characteristics Based on Monomer Graphite Fiber

HUO Haibo, ZHENG Yajuan, MA Huali, DONG Zihua, LI Qianqian, LI Mingyu, DING Pei, ZENG Fanguang

School of Materials Science and Engineering, Zhengzhou University of Aeronautics, Zhengzhou 450015, China

Received:2021-03-08 Online:2021-05-15 Published:2021-06-15

摘要/Abstract

摘要： 利用化学气相沉积(CVD)法,以甲烷为碳源在管式炉中合成了单体石墨纤维(MGF)。选取长度为3.426 mm,顶端球面半径为11.26 μm的单体石墨纤维直立于圆铜片上作为阴极,以导电ITO玻璃作为阳极,采用二极管结构在真空室中进行直流场发射测试,证实MGF的开启场强为0.477 5 V/μm。基于有限元仿真软件ANSYS进行电磁场分析,计算了MGF在不同电压下的有效发射面积。结果表明,当电压为5.36 kV时,MGF达到最大发射面积为796.226 μm²,在实验测量电压范围内,平均发射电流密度可以达到46.069 A/cm²,单体石墨纤维具有良好的场发射特性。

关键词: 单体石墨纤维, 场发射, 有效发射面积, 电流密度, 场增强因子

Abstract: Field emission cold cathode electron source has a wide range of application prospects in many vacuum electronic devices. Carbon materials suitable for cold cathode materials include carbon nanotubes, carbon microtubes and carbon fibers. Field emission characteristics based on single graphite fiber were studied. Single graphite fiber (MGF) was synthesized by chemical vapor deposition (CVD) in a tubular furnace with methane as carbon source. The DC field emission test was carried out in a vacuum chamber by building a diode structure. A single graphite fiber with a length of 3.426 mm and a spherical radius of 11.26 μm was selected and fixed on the copper plate as the cathode, and a conductive ITO glass was used as the anode. The opening field strength of MGF is confirmed to be 0.477 5 V/μm. Furthermore, the electromagnetic field was analyzed based on the simulation software of ANSYS. The effective emission area of MGF under different voltages was calculated. The results show that when the voltage is 5.36 kV, the maximum emission area of MGF is 796.226 μm² and the average emission current density can reach 46.069 A/cm² in the experimental voltage range. The monomer graphite fiber has good field emission characteristics.

Key words: monomer graphite fiber, field emission, effective emission area, current density, field enhancement factor

中图分类号:

TQ342⁺.743

霍海波, 郑亚娟, 麻华丽, 董子华, 李倩倩, 李明玉, 丁佩, 曾凡光. 基于单体石墨纤维的场发射特性研究[J]. 人工晶体学报, 2021, 50(5): 866-870.

HUO Haibo, ZHENG Yajuan, MA Huali, DONG Zihua, LI Qianqian, LI Mingyu, DING Pei, ZENG Fanguang. Field Emission Characteristics Based on Monomer Graphite Fiber[J]. JOURNAL OF SYNTHETIC CRYSTALS, 2021, 50(5): 866-870.

参考文献

[1] YANAGISAWA H, HAFNER C, DONÁ P, et al. Laser-induced field emission from a tungsten tip: optical control of emission sites and the emission process[J]. Physical Review B, 2010, 81(11): 115429.
[2] SANKARAN K J, AFSAL M, LOU S C, et al. Electron field emission enhancement of vertically aligned ultrananocrystalline diamond-coated ZnO core-shell heterostructured nanorods[J]. Small, 2014, 10(1): 179-185.
[3] CHEN S L, SHANG M H, GAO F M, et al. Extremely stable current emission of P-doped SiC flexible field emitters[J]. Advanced Science, 2016, 3(1): 1500256.
[4] CHEN J, CUI L, SUN D, et al. Enhanced field emission properties from aligned graphenes fabricated on micro-hole patterned stainless steel[J]. Applied Physics Letters, 2014, 105(21): 213111.
[5] CHEN J, YANG B, LIU X, et al. Field electron emission from pencil-drawn cold cathodes[J]. Applied Physics Letters, 2016, 108(19): 193112.
[6] SRIDHAR S, TIWARY C, VINOD S, et al. Field emission with ultralow turn on voltage from metal decorated carbon nanotubes[J]. ACS Nano, 2014, 8(8): 7763-7770.
[7] LAHIRI I, WONG J, ZHOU Z L, et al. Ultra-high current density carbon nanotube field emitter structure on three-dimensional micro-channeled copper[J]. Applied Physics Letters, 2012, 101(6): 063110.
[8] GAUTIER L A, LE BORGNE V, EL KHAKANI M A. Field emission properties of graphenated multi-wall carbon nanotubes grown by plasma enhanced chemical vapour deposition[J]. Carbon, 2016, 98: 259-266.
[9] CHEN Z, DEN ENGELSEN D, BACHMANN P K, et al. High emission current density microwave-plasma-grown carbon nanotube arrays by postdepositional radio-frequency oxygen plasma treatment[J]. Applied Physics Letters, 2005, 87(24): 243104.
[10] PARK S A, SONG E H, KANG B H, et al. Carbon nanotube field emitters on KOVAR substrate modified by random pattern[J]. Journal of Nanoparticle Research, 2015, 17(7): 318.
[11] KIM J W, JEONG J W, KANG J T, et al. Great improvement in adhesion and uniformity of carbon nanotube field emitters through reactive nanometer-scale SiC fillers[J]. Carbon, 2015, 82: 245-253.
[12] EVANS-NGUYEN T, PARKER C B, HAMMOCK C, et al. Carbon nanotube electron ionization source for portable mass spectrometry[J]. Analytical Chemistry, 2011, 83(17): 6527-6531.
[13] KRYSZTOF M, GRZEBYK T, SZYSZKA P, et al. Technology and parameters of thin mebrane-anode for MEMS transmission electron microscope[J]. J Vac Sci Technol B, 2018, 36(2):02C107.
[14] CHEN J T, YANG B J, LIM Y D, et al. Field emission cathode based on three-dimensional framework carbon and its operation under the driving of a triboelectric nanogenerator[J]. Nano Energy, 2018, 49: 308-315.
[15] LASZCZYK K U. Field emission cathodes to form an electron beam prepared from carbon nanotube suspensions[J]. Micromachines, 2020, 11(3): 260.
[16] DE JONGE N, LAMY Y, SCHOOTS K, et al. High brightness electron beam from a multi-walled carbon nanotube[J]. Nature, 2002, 420(6914): 393-395.
[17] BONARD J M, KIND H, STÖCKLI T, et al. Field emission from carbon nanotubes: the first five years[J]. Solid-State Electronics, 2001, 45(6): 893-914.
[18] COLLINS P G, ZETTL A. A simple and robust electron beam source from carbon nanotubes[J]. Applied Physics Letters, 1996, 69(13): 1969-1971.
[19] HOUDELLIER F, DE KNOOP L, GATEL C, et al. Development of TEM and SEM high brightness electron guns using cold-field emission from a carbon nanotip[J]. Ultramicroscopy, 2015, 151: 107-115.
[20] 曾凡光,一种石墨纤维及其制备方法:中国,201710317637.7[P].2019-09-17.
ZENG F G. A kind of graphite fiber and its preparation method: China, 201710317637.7[P]. 2019-09-17(in Chinese).