人工晶体学报 ›› 2017, Vol. 46 ›› Issue (7): 1333-1337.

• • 上一篇    下一篇

烧结升温速率对钛酸钡陶瓷压电性能的影响

朱强;周恒为;张超;尹红梅   

  1. 伊犁师范学院物理科学与技术学院,新疆凝聚态相变与微结构实验室,伊宁 835000;伊犁师范学院物理科学与技术学院,新疆凝聚态相变与微结构实验室,伊宁 835000;南京大学物理学院,国家固体微结构重点实验室,南京 210093
  • 出版日期:2017-07-15 发布日期:2021-01-20
  • 基金资助:
    新疆维吾尔自治区自然科学基金(2015211C296)

Effect of Sintering Heating Rate on Barium Titanate Ceramic Piezoelectric Properties

ZHU Qiang;ZHOU Heng-wei;ZHANG Chao;YING Hong-mei   

  • Online:2017-07-15 Published:2021-01-20

摘要: 采用固相反应方法在不同烧结升温速率下制备了BaTiO3陶瓷,并对陶瓷样品的晶体结构、表面形貌、介电、压电和铁电性能进行了测试和分析.结果表明:当烧结升温速率为3 ℃/min和5 ℃/min时陶瓷均为四方钙钛矿晶格结构,随升温速率的增大,四方相程度增强,材料平均晶粒尺寸减小,压电系数和铁电性能随之降低,但介电常数随之增大,当烧结升温速率为5 ℃/min介电常数最大,其值为3144.当烧结升温速率为1 ℃/min时陶瓷为正交钙钛矿晶格结构d33和Pr最大,其值为Pr=10 μC/cm2和d33=193 pC/N.

关键词: 钛酸钡陶瓷;固相反应法;升温速率;压电性能

Abstract: BaTiO3 ceramics were prepared by traditional solid state reaction method at different heating rates and the crystal structure, surface morphology, dielectric, piezoelectric and ferroelectric properties of ceramic samples were tested and analyzed.The results show that when the sintering temperature rate is 3 ℃/min and 5 ℃/min, the ceramic is tetrahedral perovskite lattice structure.With the increase of the heating rate, the tetragonal phase increases while the average grain size decreases, electrical coefficient and the ferroelectric properties decrease with it.However, the dielectric constant increases.When the sintering temperature rate is 5 ℃/min, dielectric constant is the largest with the value of 3144.When the sintering temperature rate is 1 ℃/min, the ceramic is orthorhombic perovskite lattice structure, of which the d33 and Pr is the maximum, its value is Pr =10 μC/cm2 while d33=193 pC/N.

Key words: BaTiO3 ceramics were prepared by traditional solid state reaction method at different heating rates and the crystal structure, surface morphology, dielectric, piezoelectric and ferroelectric properties of ceramic samples were tested and analyzed.The results show that when the sintering temperature rate is 3 ℃/min and 5 ℃/min, the ceramic is tetrahedral perovskite lattice structure.With the increase of the heating rate, the tetragonal phase increases while the average grain size decreases, electrical coefficient and the ferroelectric properties decrease with it.However, the dielectric constant increases.When the sintering temperature rate is 5 ℃/min, dielectric constant is the largest with the value of 3144.When the sintering temperature rate is 1 ℃/min, the ceramic is orthorhombic perovskite lattice structure, of which the d33 and Pr is the maximum, its value is Pr =10 μC/cm2 while d33=193 pC/N.