室温铁磁性Sr3YCo4O10.5+δ多晶有序化的烧结工艺及电磁性能

人工晶体学报 ›› 2021, Vol. 50 ›› Issue (6): 1082-1088.

室温铁磁性Sr₃YCo₄O_10.5+δ多晶有序化的烧结工艺及电磁性能

霍广鹏, 张晓东, 宋宏远, 惠玉玉, 杜晓丽, 陈亮维, 虞澜

昆明理工大学材料科学与工程学院,昆明 650093

收稿日期:2021-01-21 出版日期:2021-06-15 发布日期:2021-07-08
通讯作者: 虞澜,博士,教授。E-mail:973819774@qq.com
作者简介:霍广鹏(1995—),男,山西省人,硕士研究生。E-mail:1547974403@qq.com
基金资助:
国家自然科学基金(51962017,51462017)

Sintering Process and Electrical Magnetic Properties of Ordered Room Temperature Ferromagnetism Sr₃YCo₄O_10.5+_δ Polycrystals

HUO Guangpeng, ZHANG Xiaodong, SONG Hongyuan, HUI Yuyu, DU Xiaoli, CHEN Liangwei, YU Lan

Faculty of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093, China

Received:2021-01-21 Online:2021-06-15 Published:2021-07-08

摘要/Abstract

摘要： 采用固相反应法制备了不同烧结温度(950~1 180 ℃)、烧结时间、烧结次数共7种工艺的Sr₃YCo₄O_10.5+_δ多晶块材,通过热分析、XRD、SEM确定了有序化相变和最佳烧结工艺(1 180 ℃/24 h+1 180 ℃/24 h),并研究了多晶的电磁性能。结果表明,964 ℃完全晶化的四方相Sr₃YCo₄O_10.5在1 042 ℃吸氧(δ)完成有序化,生成Sr₃YCo₄O_10.5+_δ,而1 100 ℃和1 180 ℃烧结的样品均出现(103)、(215)超结构峰,验证了其结构的有序性。块材均呈半导体电输运行为,二次烧结晶格完整性提高,晶粒长大,300 K时电阻率仅为0.06 Ω·cm,居里温度(T_c)~335 K,零场冷曲线(ZFC)上的Hopkinson峰源于低温时被冻结的磁矩随温度升高转向磁场方向,磁化强度在298 K达到最大,随后受热扰动的影响减小。室温铁磁性源于有序结构导致的中自旋或高自旋态Co³⁺的e_g轨道有序。

关键词: Sr₃YCo₄O_10.5+_δ多晶, 固相反应法, 磁性能, Hopkinson峰, 室温铁磁性

Abstract: Sr₃YCo₄O_10.5+_δ polycrystalline bulks were prepared by the solid state reaction of 7 processes with different sintering temperatures (950~1 180 ℃), sintering time and sintering times. Based on thermal analysis, XRD and SEM, order phase transition and optimal sintering process (1 180 ℃/24 h+1 180 ℃/24 h) were determined, then electrical magnetic properties of polycrystals were inverstigated. The results show that the tetragonal Sr₃YCo₄O_10.5 fully crystallized at 964 ℃ and formed the ordering Sr₃YCo₄O_10.5+_δ by absorbs oxygen (δ) at 1 042 ℃. Samples sintered at 1 100 ℃ and 1 180 ℃ show superstructure peaks of (103) and (215), which verifies the order of polycrystalline structure. The bulks exhibit semiconductor behavior, secondary sintering improve the lattice integrity, grain growth and resistivity is only 0.06 Ω·cm at 300 K, Curie temperature (T_c)~335 K. Hopkinson peak on the zero field colded (ZFC) curve from the fact that the frozen magnetic moments at low temperature turn to the direction of the magnetic field as the temperature rises, the magnetization reaches the maximum at 298 K, and then decreases under the thermal disturbance. Room temperature ferromagnetism originates from the e_g orbitals ordering of the middle spin or high spin state Co³⁺ caused by the ordered structure.

Key words: Sr₃YCo₄O_10.5+δ polycrystal, solid state reaction, magnetic property, Hopkinson peak, room temperature ferromagnetism

中图分类号:

TM27

霍广鹏, 张晓东, 宋宏远, 惠玉玉, 杜晓丽, 陈亮维, 虞澜. 室温铁磁性Sr₃YCo₄O_10.5+δ多晶有序化的烧结工艺及电磁性能[J]. 人工晶体学报, 2021, 50(6): 1082-1088.

HUO Guangpeng, ZHANG Xiaodong, SONG Hongyuan, HUI Yuyu, DU Xiaoli, CHEN Liangwei, YU Lan. Sintering Process and Electrical Magnetic Properties of Ordered Room Temperature Ferromagnetism Sr₃YCo₄O_10.5+_δ Polycrystals[J]. JOURNAL OF SYNTHETIC CRYSTALS, 2021, 50(6): 1082-1088.

参考文献

[1] WITHERS R L, JAMES M, GOOSSENS D J.Atomic ordering in the doped rare earth cobaltates Ln_0.33Sr_0.67CoO_3-_δ (Ln=Y³⁺, Ho³⁺ and Dy³⁺)[J].Journal of Solid State Chemistry, 2003, 174(1):198-208.
[2] ISTOMIN S Y, GRINS J, SVENSSON G, et al.Crystal structure of the novel complex cobalt oxide Sr_0.7Y_0.3CoO_2.62[J].Chemistry of Materials, 2003, 15(21):4012-4020.
[3] LINDBERG F, DROZHZHIN O A, ISTOMIN S Y, et al.Synthesis and characterization of Sr_0.75Y_0.25Co_1-xM_xO_2.625+δ (M=Ga, 0.125≤x≤0.500 and M=Fe, 0.125≤x≤0.875)[J].Journal of Solid State Chemistry, 2006, 179(5):1434-1444.
[4] ISTOMIN S Y, DROZHZHIN O A, NAPOLSKY P S, et al.Thermal expansion behavior and high-temperature transport properties of Sr₃YCo_4-xFe_xO_10.5+y, x=0.0, 1.0, 2.0 and 3.0[J].Solid State Ionics, 2008, 179(21/22/23/24/25/26):1054-1057.
[5] KOBAYASHI W, ISHIWATA S, TERASAKI I, et al.Room-temperature ferromagnetism inSr_1-xY_xCoO_3-δ(0.2≤x≤0.25)[J].Physical Review B, 2005, 72(10):104408.
[6] KOBAYASHI W, YOSHIDA S, TERASAKI I.High-temperature metallic state of room-temperature ferromagnet Sr_1-xY_xCoO_3-δ[J].Journal of the Physical Society of Japan, 2006, 75(10):103702.
[7] KOBAYASHI W, YOSHIDA S, TERASAKI I.Unusual impurity effect on room-temperature ferromagnet Sr₃YCo₄O_10.56[J].Progress in Solid State Chemistry, 2007, 35(2/3/4):355-360.
[8] ZHANG Y F, SASAKI S, YANAGISAWA O, et al.Magnetic properties of oxygen deficient Y_0.33Sr_0.67CoO_3-δ[J].Acta Physica Polonica A, 2007, 111(1):79-86.
[9] NAKAO H, MURATA T, BIZEN D, et al.Orbital ordering of intermediate-spin state of Co³⁺ in Sr₃YCo₄O_10.5[J].Journal of the Physical Society of Japan, 2011, 80(2):023711.
[10] SHEPTYAKOV D V, POMJAKUSHIN V Y, DROZHZHIN O A, et al.Correlation of chemical coordination and magnetic ordering in Sr₃YCo₄O_10.5+δ(δ=0.02 and 0.26)[J].Physical Review B, 2009, 80(2):024409.
[11] WANG Y J, ZHU X B, DAI J M, et al.Simple chemical solution deposition of Sr_0.775Y_0.225CoO_3-δ film with room-temperature ferromagnetism[J].Journal of the American Ceramic Society, 2010, 93(11):3542-3544.
[12] KHALYAVIN D D, CHAPON L C, SUARD E, et al.Complex room-temperature ferrimagnetism induced by zigzag stripes of oxygen vacancies inSr₃YCo₄O_10+δ[J].Physical Review B, 2011, 83(14):140403.
[13] BETTIS J L Jr, XIANG H J, WHANGBO M H.Origin of the room-temperature ferromagnetism in Sr₃YCo₄O_10+δ (0.5<δ<1.0):formation of ferromagnetic spin bags in the oxygen-rich perovskite layers[J].Chemistry of Materials, 2012, 24(16):3117-3119.
[14] YOSHIDA S, KOBAYASHI W, NAKANO T, et al.Chemical and physical pressure effects on the magnetic and transport properties of the A-site ordered perovskite Sr₃YCo₄O_10.5[J].Journal of the Physical Society of Japan, 2009, 78(9):094711.
[15] NONG N V, PRYDS N.Thermoelectric properties and microstructure of modified novel complex cobalt oxides Sr₃RECo₄O_10.5 (RE=Y, Gd)[C]//Thessaloniki, Greece.AIP, 2012:339-342.
[16] FUKUSHIMA S, SATO T, AKAHOSHI D, et al.Order-disorder effect of A-site and oxygen-vacancy on magnetic and transport properties of Y_1/4Sr_3/4CoO_3-δ[J].Journal of the Physical Society of Japan, 2009, 78(6):064706.
[17] 刘相果,彭晓东,谢卫东,等.SrCO₃的热分解动力学及其影响因素[J].材料研究学报,2005,19(3):287-292.
LIU X G, PENG X D, XIE W D, et al.Decomposition kinetics and its influencing factors SrCO₃ of with high purity[J].Chinese Journal of Materials Research, 2005, 19(3):287-292(in Chinese).
[18] YAN J Q, ZHOU J S, GOODENOUGH J B.Ferromagnetism in LaCoO₃[J].Physical Review B, 2004, 70:014402.
[19] TROYANCHUK I O, BUSHINSKY M V, DOBRYANSKII V M, et al.First-order magnetic phase transition in layered Sr₃YCo₄O_10.5+δ-type cobaltites[J].JETP Letters, 2012, 94(12):849-852.
[20] TROYANCHUK I O, BUSHINSKY M V, TERESHKO N V, et al.Ferromagnet-antiferromagnet transition in layered perovskites of Sr₃YCo₄O_10.5 type[J].Materials Research Express, 2018, 6(2):026105.
[21] MARIK S, MOHANTY P, SINGH D, et al.Moderate magnetic field induced large exchange bias effect in ferrimagnetic 314-Sr₃YCo₄O_10.5material[J].Journal of Physics D:Applied Physics, 2018, 51(6):065006.

室温铁磁性Sr₃YCo₄O_10.5+δ多晶有序化的烧结工艺及电磁性能

Sintering Process and Electrical Magnetic Properties of Ordered Room Temperature Ferromagnetism Sr₃YCo₄O_10.5+_δ Polycrystals

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	马国斌, 杨松, 徐蕾, 郭凯鑫, 王旭. Gd³⁺、Co³⁺共掺杂铁酸铋薄膜多铁性增强及带隙调谐[J]. 人工晶体学报, 2021, 50(5): 851-857.
[2]	许文君;梁进闯;周恒为;黄以能;陈云飞;尹红梅. 烧结温度对(Ba0.85 Ca0.15)(Ti0.9 Hf0.1)O3陶瓷压电性能的影响[J]. 人工晶体学报, 2019, 48(5): 955-960.
[3]	杨帅;李国华. 添加剂对锌铝尖晶石晶粒尺寸的影响[J]. 人工晶体学报, 2019, 48(3): 409-412.
[4]	王晓军;田澍. 稀土Tb掺杂对BiFeO3纳米颗粒结构及磁性能的影响[J]. 人工晶体学报, 2018, 47(9): 1954-1959.
[5]	杜立辉;张家敏;杨军;王静哲;易健宏;甘国友;严继康;杜景红. pH值对水热合成纳米锰锌铁氧体生长和磁性能影响[J]. 人工晶体学报, 2018, 47(10): 2089-2093.
[6]	韩基铄;李国华;李国义. 添加剂促进锌铝尖晶石生成机理研究[J]. 人工晶体学报, 2018, 47(10): 2138-2141.
[7]	常靖宇;孔迪;马振振;刘先松;李明玲. 溶胶-凝胶自燃烧法制备Ba(NiMg)0.2AlxFe11.4-xO19的结构与磁性能[J]. 人工晶体学报, 2017, 46(9): 1786-1790.
[8]	王卫伟;于欢;姚佳良;张爱娟. 磁性LDHs复合材料的制备及可见光光催化性能研究[J]. 人工晶体学报, 2017, 46(9): 1833-1837.
[9]	朱强;周恒为;张超;尹红梅. 烧结升温速率对钛酸钡陶瓷压电性能的影响[J]. 人工晶体学报, 2017, 46(7): 1333-1337.
[10]	张宗阳;刘先松;张丛;李浩浩;孟祥雨;刘超成. Fe80.8Si7.2B6Nb5Cu非晶/纳米晶磁粉芯软磁性能研究[J]. 人工晶体学报, 2017, 46(7): 1338-1342.
[11]	谈文鹏;虞澜;潘鹏;宋世金;刘丹丹. Sr3YCo4-xMgxO10.5+δ(0≤x≤0.04)多晶的制备和热电输运性质研究[J]. 人工晶体学报, 2017, 46(6): 957-961.
[12]	曹利华;陈拥军;李建保;骆丽杰;徐智超;张弨. 氯化亚铁催化制备硼碳氮纳米管[J]. 人工晶体学报, 2017, 46(3): 562-565.
[13]	胡建力;虞澜;杜小丽;宋世金. 室温铁磁Sr3YCo4O10.5+δ多晶的制备及其性能研究[J]. 人工晶体学报, 2017, 46(2): 238-242.
[14]	康冶;虞澜;杜小丽;樊堃;宋世金;谭红琳;陈亮维;杨森. 室温铁磁Sr4-xErxCo4O10.5+δ(0.6≤x≤1.2)多晶电输运和磁性能[J]. 人工晶体学报, 2016, 45(5): 1168-1173.
[15]	蔡君德;傅仁利;杨扬;徐越;费盟;刘超;杨芳. (Ni1/3Nb2/3)1-xTixO2微波介质陶瓷的组织结构及微波介电性能[J]. 人工晶体学报, 2016, 45(3): 618-622.