Research Progress on Magnesium Aluminate Spinel Transparent Ceramic

Abstract

Abstract: Magnesium aluminate spinel, as an advanced transparent ceramic material, has excellent properties such as wide transmission band, high transmittance, isotropy, high hardness, high strength, high thermal conductivity, high thermal shock resistance, high corrosion resistance, and high-temperature stability. It can be widely applicated to the fields of national defense security and key high-performance equipment, such as infrared guidance windows, high Mach aircraft domes, transparent armor and photoelectronic equipment windows in extreme environments. In this paper, the basic properties and the development of magnesium aluminate spinel transparent ceramic are summarized, the research and development work of Sinoma Sythentic Crystal Co., Ltd. over the last three decades are focused on, including high-purity spinel powder synthesis, magnesium aluminate spinel transparent ceramic forming and sintering process, the performance and application.The difficulties encountered in material development and the challenges faced in the application development are analyzed. Based on these, the research directions and methods are considered, its application and development are prospected.

Key words: magnesium aluminate spinel, transparent ceramics, powder synthesis, forming and sintering process, property, application

CLC Number:

TQ174.75⁺8.23

LEI Muyun, LI Zhen, ZHANG Wei, PANG Zhenli, SHI Shuangshuang, HUANG Cunxin. Research Progress on Magnesium Aluminate Spinel Transparent Ceramic[J]. JOURNAL OF SYNTHETIC CRYSTALS, 2023, 52(12): 2108-2124.

References

[1] KINGERY W D, BOWEN H K, UHIMANN D R. 陶瓷导论[M]. 2版. 北京:北京高等教育出版社, 2010: 51-52.
KINGERY W D, BOWEN H K, UHIMANN D R. Introduction to ceramics[M]. 2nd ed. Beijing: Higher Education Press, 2010: 51-52 (in Chinese).
[2] RUBAT DU MERAC M, KLEEBE H J, MÜLLER M M, et al. Fifty years of research and development coming to fruition; unraveling the complex interactions during processing of transparent magnesium aluminate (MgAl₂O₄) spinel[J]. Journal of the American Ceramic Society, 2013, 96(11): 3341-3365.
[3] COLE R L. Transparent alumina and method of preparation: US, 3026210[P]. 1962-03-20.
[4] RICE R W. Hot-pressing of MgO with NaF[J]. Journal of the American Ceramic Society, 1971, 54(4): 205-207.
[5] GRESKOVICH C, WOODS K N. Fabrication of transparent ThO₂ doped In₂O₃[J]. Am Ceram Soc Bull, 1973, 52 (5): 473-478.
[6] LEFEVER R A, MATSKO J. Transparent yttrium oxide ceramics[J]. Materials Research Bulletin, 1967, 2(9): 865-869.
[7] MCCAULEY J W, CORBIN N D. Phase relations and reaction sintering of transparent cubic aluminum oxynitride spinel (ALON)[J]. Journal of the American Ceramic Society, 1979, 62(9/10): 476-479.
[8] CORBIN N, MCCAULEY J. Nitrogen-stabilized aluminum oxide spinel (ALON)[C]. SPIE, 1982.
[9] BRATTON R J. Translucent sintered MgAl₂O₄[J]. Journal of the American Ceramic Society, 1974, 57(7): 283-286.
[10] ROY D W. Hot-pressed MgAl₂O₄ for UV, visible, and IR optical requirements[C]. Emering Optical Materials SPIE, 1981, 297: 13-18.
[11] DE G, VAN DIJK H J A. Translucent Y₃Al₅O₁₂ ceramics[J]. Materials Research Bulletin, 1984, 19(12): 1669-1674.
[12] SEKITA M, HANEDA H, SHIRASAKI S, et al. Optical spectra of undoped and rare-earth-(Pr, Nd, Eu, and Er) doped transparent ceramic Y₃Al₅O₁₂[J]. Journal of Applied Physics, 1991, 69(6): 3709-3718.
[13] CUSANO D A, GRESKOVICH C D, DIBIANCA F A. Rare-earth-doped yttria-gadolinia ceramic scintillators: US4421671[P]. 1983-12-20.
[14] GRESKOVICH C, CUSANO D, DIBIANCA F. Rare-earth doped yttria-gadolinia ceramic scintillators by vacuum hot pressing: US4466930[P]. 1984.
[15] CUSANO D A, GRESKOVICH C D, DIBIANCA F A. Method for sintering high density yttria-gadolinia ceramic scintillators: US4518545[P]. 1985-05-21.
[16] YAMADA H, SUZUKI A, UCHIDA Y, et al. A scintillator Gd₂O₂S∶Pr, Ce, F for X-ray computed tomography[J]. Journal of the Electrochemical Society, 1989, 136(9): 2713-2716.
[17] ITO Y, YAMADA H, YOSHIDA M, et al. Hot isostatic pressed Gd₂O₂S∶Pr, Ce, F translucent scintillator ceramics for X-ray computed tomography detectors[J]. Japanese Journal of Applied Physics, 1988, 27(8A): L1371.
[18] YOSHIDA M, NAKAGAWA M, FUJII H, et al. Application of Gd₂O₂S ceramic scintillator for X-ray solid state detector in X-ray CT[J]. Japanese Journal of Applied Physics, 1988, 27(8A): L1572.
[19] 谢菊芳, 张端明, 王世敏, 等. 透明PLZT电光陶瓷材料的制备及应用研究进展[J]. 功能材料, 1998, 29(1): 1-7.
XIE J F, ZHANG D M, WANG S M, et al. Progress on the fabrication and applications of transparent electrooptic PLZT ceramic materials[J]. Journal of Functional Materials, 1998, 29(1): 1-7 (in Chinese).
[20] 黄存新. 光学透明多晶尖晶石的制备及应用研究[D]. 北京: 清华大学, 2005.
HUANG C X. Preparation and application of optically transparent polycrystalline spinel[D]. Beijing: Tsinghua University, 2005 (in Chinese).
[21] MEHROTRA R C, GOEL S, GOEL A B, et al. Preparation and characterization of some volatile double isopropoxides of aluminum with alkaline earth metals[J]. Inorganica Chimica Acta, 1978, 29: 131-136.
[22] GENTILMAN R L. Fusion-casting of transparent spinel[J]. American Ceramic Society Bulletin, 1981: 906.
[23] BECHER P F. Press-forged Al₂O₃-rich spinel crystals for IR application[J]. Am Ceram Soc Bull, 1977, 56(11): 1015–1017.
[24] BRATTON R J. Characterization and sintering of reactive MgAl₂O₄ spinel[J]. Ceramic Bulletin, 1969, 48(11): 1069-1075.
[25] BRATTON R J, TERWILLIGER G R, HO S M. Densification phenomena in the hot-pressing of spinel[J]. Journal of Materials Science, 1972, 7(12): 1363-1368.
[26] THOMAS M E, JOSEPH R I, TROPF W J. Infrared transmission properties of sapphire, spinel, yttria, and ALON as a function of temperature and frequency[J]. Applied Optics, 1988, 27(2): 239-245.
[27] ROY D W, HASTERT J L, COUBROUGH L E, et al. Method for producing transparent polycrystalline body with high ultraviolet transmittance: US5244849[P]. 1993-09-14.
[28] ROY D W, HASTERT J L. Transparent polycrystalline body with high ultraviolet transmittance: US5001093[P]. 1991-03-19.
[29] ROY D W, HASTERT J L. Dome and window for missiles and launch tubes with high ultraviolet transmittance: US4930731[P]. 1990-06-05.
[30] ROY D W, HASTERT J L, GREEN K E, et al. Metallized spinel with high transmittance and process for producing: US5082739[P]. 1992-01-21.
[31] ROY D W, HASTERT J L, et al. Application of transparent polycrystalline body with high ultraviolet transmittanc e: US4983555[P]. 1991-01-08.
[32] SHIBATA K, NAKAMURA H. Method of producing a light-transmitting spinel sintered body: US5152940[P]. 1992-10-06.
[33] GILDE G A, PATEL P J, PATTERSON M. Comparison of hot-pressing, rate-controlled sintering, and microwave sintering of magnesium aluminate for optical applications[C]//AeroSense ′99. Proc SPIE 3705, Window and Dome Technologies and Materials VI, Orlando, FL, USA. 1999, 3705: 94-104.
[34] BOCH P, BERGEZ P. Fabrication of transparent MgAl₂O₄ ceramics[C]. Ceramics Today-Tomorrow’s Ceramics, Elsevier Science Publishers B.V., 1991.
[35] ROY R, AGRAWAL D K. Transparent armor materials[C]. Proceedings of DARPA/ARL/ARO Transparent Armor Materials Workshop, Annapolis, MD, 16-17, 1998.
[36] 董存新, 彭载学, 刘德铭, 等. 一种透明多晶尖晶石的制备方法: CN1049881C[P]. 1996-07-31.
DONG C X, PENG Z X, LIU D M, et al. Preparation method of transparent polycrystalline spinel: CN1049881C. 1996-07-31 (in Chinese).
[37] THOMAS J M, THOMAS M H,JOSEPH M W, et al. Recent adance spinel optical ceramic[J].Proceedings of SPIE, 2005,786:64.
[38] KIRSCH J C, LINDBERG W R, HARRIS D C, et al. Tri-mode seeker dome considerations[C]//Defense and Security. Proc SPIE 5786, Window and Dome Technologies and Materials IX, Orlando, Florida, USA. 2005, 5786: 33-40.
[39] SANGHERA J S, ROCK B, VILLALOBOS G, et al. Highly transparent spinel windows by microwave sintering[C]//SPIE Defense + Security. Proc SPIE 9453, Window and Dome Technologies and Materials XIV, Baltimore, MD, USA. 2015, 9453: 945302.
[40] SPILMAN J, VOYLES J, NICK J, et al. Manufacturing process scale-up of optical grade transparent spinel ceramic at ArmorLine Corporation[C]//SPIE Defense, Security, and Sensing. Proc SPIE 8708, Window and Dome Technologies and Materials XIII, Baltimore, Maryland, USA. 2013, 8708: 36-45.
[41] PATTERSON MC L, CAIAZZA J E, ROY D W. Transparent spinel development[J]. Proceedings of SPIE, 2000, 4102: 59-68.
[42] 付萍, 吕文中. 透明MgAl₂O₄陶瓷制备工艺研究进展[J]. 电子元件与材料, 2011, 30(11): 77-81.
FU P, LÜ W Z. Research progress of transparent MgAl₂O₄ ceramic on preparation process[J]. Electronic Components and Materials, 2011, 30(11): 77-81 (in Chinese).
[43] MORITA K, KIM B N, HIRAGA K, et al. Fabrication of transparent MgAl₂O₄ spinel polycrystal by spark plasma sintering processing[J]. Scripta Materialia, 2008, 58(12): 1114-1117.
[44] WANG C, ZHAO Z. Transparent MgAl₂O₄ ceramic produced by spark plasma sintering[J]. Scripta Materialia, 2009, 61(2): 193-196.
[45] MEIR S, KALABUKHOV S, FROUMIN N, et al. Synthesis and densification of transparent magnesium aluminate spinel by SPS processing[J]. Journal of the American Ceramic Society, 2009, 92(2): 358-364.
[46] 王修慧. 镁铝尖晶石、钇铝石榴石粉体的制备研究[D]. 沈阳: 东北大学, 2009.
WANG X H. Study on preparation of magnesium aluminum spinel and yttrium aluminum garnet powder[D].Shenyang: Northeastern University, 2009 (in Chinese).
[47] 刘炜. Mg-Al双金属醇盐的性质、水解机理及尖晶石粉体制备的研究[D]. 大连: 大连交通大学, 2005.
LIU W. Study on properties, hydrolysis mechanism and preparation of spinel powder of Mg-Al bimetallic alkoxide[D].Dalian: Dalian Jiaotong University, 2005 (in Chinese).
[48] 曹冬鸽. 高纯镁铝尖晶石粉体的制备与研究[D]. 大连: 大连交通大学, 2007.
CAO D G. Preparation and study of high purity magnesia-alumina spinel powder[D].Dalian: Dalian Jiaotong University, 2007 (in Chinese).
[49] 黄存兵, 卢铁城, 雷牧云, 等. MgO·nAl₂O₃透明陶瓷的制备及其物性[J]. 材料研究学报, 2006, 20(1): 49-53.
HUANG C B, LU T C, LEI M Y, et al. Preparation and properties of non-stoichiometric MgO·nAl₂O₃ transparent ceramics[J]. Chinese Journal of Materials Research, 2006, 20(1): 49-53 (in Chinese).
[50] 齐建起, 卢铁城, 常相辉, 等. MgAl₂O₄纳米透明陶瓷的制备及其透明机理[J]. 材料研究学报, 2006, 20(4): 367-371.
QI J Q, LU T C, CHANG X H, et al. Investigation on preparation and transparent mechanism of MgAl₂O₄ transparent nario-ceramics[J]. Chinese Journal of Materials Research, 2006, 20(4): 367-371 (in Chinese).
[51] 李祯, 雷牧云, 王立弟. 增强型镁铝尖晶石透明陶瓷的制备[J]. 陶瓷学报, 2012, 33(4): 488-491.
LI Z, LEI M Y, WANG L D. Preparation of enhanced transparent magnesia-alumina spinel ceramics[J]. Journal of Ceramics, 2012, 33(4): 488-491 (in Chinese).
[52] LU T C, WANG X J, CHENG B X, et al. Novel visible-band transparent ceramic laser material Mn∶MgAl₂O₄[J]. Key Engineering Materials, 2007, 336/337/338: 1229-1232.
[53] 张珂. 纳米镁铝尖晶石透明陶瓷制备工艺研究[D]. 西安: 西安电子科技大学, 2011.
ZHANG K. Study on preparation technology of nano-magnesia-alumina spinel transparent ceramics[D].Xi′an: Xidian University, 2011 (in Chinese).
[54] 付萍. 尖晶石基透明陶瓷的制备及其光学、微波介电性能的研究[D]. 武汉: 华中科技大学, 2014.
FU P. Preparation and optical and microwave dielectric properties of spinel-based transparent ceramics[D].Wuhan: Huazhong University of Science and Technology, 2014 (in Chinese).
[55] PATTERSON M, CAIAZZA J E, ROY D W. Transparent spinel development[C]//International Symposium on Optical Science and Technology. Proc SPIE 4102, Inorganic Optical Materials II, San Diego, CA, USA. 2000, 4102: 59-68.
[56] LEI M Y, HUANG C X, SUN J L. Effect of HIP on the properties and microstructure of transparent polycrystalline spinel[M]//Key Engineering Materials. Stafa: Trans Tech Publications Ltd., 2007: 1200-1202.
[57] 王康, 田洪翼, 杨威, 等. 镁铝尖晶石透明陶瓷的研究进展[J]. 现代技术陶瓷, 2023, 44(2): 77-116.
WANG K, TIAN H Y, YANG W, et al. A review on magnesium aluminate spinel transparent ceramics[J]. Advanced Ceramics, 2023, 44(2): 77-116 (in Chinese).
[58] 黄存新, 雷牧云, 彭载学, 等. 透明多晶尖晶石的光学和物理性能[J]. 人工晶体学报, 2001, 30(1): 67-71.
HUANG C X, LEI M Y, PENG Z X, et al. Optical and mechanical properties of transparent polycrystalline spinel[J]. Journal of Synthetic Crystals, 2001, 30(1): 67-71 (in Chinese).
[59] 雷牧云, 黄存新, 宋庆海, 等.透明多晶尖晶石的制备及应用研究[C]. 特种陶瓷及金属封接技术基础和应用研讨会论文集, 2005, 4:19-22.
LEI M Y, HUANG C X, SONG Q H, et al. Study on the fabrication and application of transparent polycrystalline spinel[C]. Proceedings of the Symposium on Basic and Application of Special ceramic and Metal sealing technology, 2005, 4:19-22(in Chinese).
[60] 雷牧云, 洪冬梅, 闻芳, 等. 透明尖晶石陶瓷的透过性能研究[J]. 红外与激光工程, 2007, 36(S2): 620-623.
LEI M Y, HONG D M, WEN F, et al. Transparent propertiy of transparent ceramic spinel[J]. Infrared and Laser Engineering, 2007, 36(S2): 620-623 (in Chinese).
[61] 闻芳, 何庭秋, 雷牧云, 等. 透明陶瓷镁铝尖晶石MgAl₂O₄耐酸碱性能的初步研究[J]. 腐蚀与防护, 2009, 30(1): 36-38.
WEN F, HE T Q, LEI M Y, et al. Corrosion-resistance of transparent ceramic spinel MgAl₂O₄[J]. Corrosion & Protection, 2009, 30(1): 36-38 (in Chinese).
[62] 贺琦. 红外光学材料及金刚石涂层(薄膜)冲蚀磨损研究[D]. 北京: 北京科技大学, 2007.
HE Q. Study on erosion wear of infrared optical materials and diamond coating (film) [D]. Beijing: University of Science and Technology Beijing, 2007 (in Chinese).
[63] 何捷, 林理彬, 卢勇, 等. γ辐射及退火MgAl₂O₄透明陶瓷光谱特性研究[J]. 人工晶体学报, 2002, 31(1): 63-66.
HE J, LIN L B, LU Y, et al. Study on optical spectra of transparent MgAl₂O₄ ceramics treated with γ-irradiation and annealing[J]. Journal of Synthetic Crystals, 2002, 31(1): 63-66 (in Chinese).
[64] WHITE G S, LEE K H, CRAWFORD J H. Effects of γ-irradiation upon the optical behavior of spinel[J]. Physica Status Solidi (a), 1977, 42(2): K137-K141.
[65] KINOSHITA C. Radiation-induced microstructural change in ceramic materials[J]. Journal of Nuclear Materials, 1992, 191/192/193/194: 67-74.
[66] 余本海, 戴能利, 李玉华, 等. 飞秒激光烧蚀MgAl₂O₄透明陶瓷的实验研究[J]. 无机材料学报, 2007, 22(2): 328-332.
YU B H, DAI N L, LI Y H, et al. Experimental study on femtosecond laser ablation of MgAl₂O₄ transparent ceramics[J]. Journal of Inorganic Materials, 2007, 22(2): 328-332 (in Chinese).
[67] 黄亦工, 张巨先. 镁铝尖晶石陶瓷的高温Mo-Mn金属化机理研究[C]//真空电子与专用金属材料、陶瓷—金属封接专辑. 济南, 2012: 22-25.
[68] GENTILMAN R L. Current and emerging materials for 3-5 micron IR transmission[C]//30th Annual Technical Symposium. Proc SPIE 0683, Infrared and Optical Transmitting Materials, San Diego, USA. 1986, 0683: 2-11.
[69] 黄秋, 陈亦庆, 高志峰, 等. 红外导引头整流罩技术研究[J]. 应用光学, 2009, 30(5): 840-843.
HUANG Q, CHEN Y Q, GAO Z F, et al. Consideration to radome technology for IR seeker[J]. Journal of Applied Optics, 2009, 30(5): 840-843 (in Chinese).
[70] 赵洪卫, 侯天晋, 朱斌. 尖晶石整流罩气动效应的试验研究[J]. 红外与激光工程, 2012, 41(2): 297-303.
ZHAO H W, HOU T J, ZHU B. Experimental research of aerodynamic effects of spinel domes[J]. Infrared and Laser Engineering, 2012, 41(2): 297-303 (in Chinese).
[71] WANG Q H, CHENG J B, LIN Z L. YAG phosphor screen for projection CRT[J]. Electronics Letters, 1998, 34(14): 1420.
[72] WANG Q H, CHENG J B, LIN Z L, et al. A high-luminance and high-resolution CRT for projection HDTV display[J]. Journal of the Society for Information Display, 1999, 7(3): 183-186.
[73] 沈德忠, 黄存新, 彭载学, 等. 彩色投影电视阴极射线管发光面板基片: CN1053062C[P]. 2000-05-31.
SHEN D Z, HUANG C X, PENG Z X, et al. Color projection television cathode ray tube luminescent panel substrate: CN1053062C[P]. 2000-05-31.
[74] SHEN D Z, HUANG C X, PENG Z X, et al. Luminous face-plate of a color projection cathode ray tube and the substrate for manufacturing the same:US, 6489715[P]. 2002.
[75] 何锡源, 张旭, 张福甲. 封装用高热导率硅胶性能的研究[J]. 光电子技术, 2011, 31(2): 141-144.
HE X Y, ZHANG X, ZHANG F J. Thermally conductive silicone in LED package application[J]. Optoelectronic Technology, 2011, 31(2): 141-144 (in Chinese).
[76] REGINA B, GERD O, DAVID A, et al. A light emtting diode device comprising a luminescent substrate that performs phosphor conversion: US, AU7720900A[P], 2001-04-30.
[77] FUJITA S, YOSHIHARA S, SAKAMOTO A, et al. YAG glass-ceramic phosphor for white LED (I): background and development[C]//Fifth International Conference on Solid State Lighting", "SPIE Proceedings. San Diego, California, USA. SPIE, 2005, 5491: 549111-17.
[78] DE G J,KOP T A,KOP T, et al. Phosphor of doted yttrium-aluminum-garnet type embedded in ceramic matrix comprising non-luminescent polycrystalline alumina useful in light emitting element: US, WO2006097876-A1[P], 2006-09-21.
[79] 苏锵, 谢鸿波, 方福波, 等. 一种YAG晶片式白光发光二极管及其封装方法: CN1815765A[P]. 2006-08-09.
SU Q, XIE H B, FANG F B, et al. A YAG chip type white light emitting diode and its packaging method: CN1815765A. 2006-08-09 (in Chinese).
[80] 朱学绘, 范广涵, 何安和, 等. SiO₂-YAG∶Ce³⁺玻璃荧光体的制备及其白光LED的封装[J]. 华南师范大学学报(自然科学版), 2010, 42(1): 62-66.
ZHU X H, FAN G H, HE A H, et al. SiO₂-YAG∶Ce³⁺glass phosphor prepared for white led packaging[J]. Journal of South China Normal University (Natural Science Edition), 2010, 42(1): 62-66 (in Chinese).
[81] 贺龙飞, 范广涵, 雷牧云, 等. 白光LED用新型MgAl₂O₄/Ce∶YAG透明陶瓷的发光性能[J]. 发光学报, 2013, 34(2): 133-138.
HE L F, FAN G H, LEI M Y, et al. Luminescent properties of new MgAl₂O₄/Ce∶YAG transparent ceramics for white LED applications[J]. Chinese Journal of Luminescence, 2013, 34(2): 133-138 (in Chinese).
[82] 雷牧云, 娄载亮, 李祯, 等. MgAl₂O₄透明荧光陶瓷用于白光LED的初步研究[J]. 真空电子技术, 2011(2): 43-46.
LEI M Y, LOU Z L, LI Z, et al. Study on MgAl₂O₄ transparent phosphor ceramic used in white LED[J]. Vacuum Electronics, 2011(2): 43-46 (in Chinese).
[83] 雷牧云,娄载亮, 夏勋力, 等. 透明荧光陶瓷用于白光LED的研究[C]//重庆:2011中国功能材料科技与产业高层论坛论文集(第一卷), 2011: 263-267.
LEI M Y, LOU Z L, XIA X L, et al. Research on transparent fluorescent ceramics used in white LED//Chongqing: China Functional Materials Science and Technology and Industry Forum Proceedings (Volume 1), 2011: 263-267.
[84] 雷牧云, 李祯, 贺龙飞, 等. 白光LED用MgAl₂O₄荧光透明陶瓷的制备及性能[J]. 硅酸盐通报, 2013, 32(2): 299-303.
LEI M Y, LI Z, HE L F, et al. Preparation and properties of the MgAl₂O₄ transparent phosphor ceramic for white LED applications[J]. Bulletin of the Chinese Ceramic Society, 2013, 32(2): 299-303 (in Chinese).
[85] 胡维康, 黄新友. MgAl₂O₄透明陶瓷制备工艺研究进展[J]. 中国陶瓷, 2022, 58(11): 1-8.
HU W K, HUANG X Y. Research progress in the preparation process of MgAl₂O₄ transparent ceramics[J]. China Ceramics, 2022, 58(11): 1-8 (in Chinese).
[86] 武小娟, 王明远, 张翼飞, 等. MgAl₂O₄透明陶瓷粉体的研究进展[J]. 硅酸盐通报, 2016, 35(1): 137-140.
WU X J, WANG M Y, ZHANG Y F, et al. Research progress of MgAl₂O₄ transparent ceramic powder[J]. Bulletin of the Chinese Ceramic Society, 2016, 35(1): 137-140 (in Chinese).
[87] 张蔓, 刘建华, 周俊文. 镁铝尖晶石烧结致密化用烧结助剂的研究进展[J]. 昆明理工大学学报(自然科学版), 2021, 46(4): 11-17.
ZHANG M, LIU J H, ZHOU J W. Research progress of sintering aids for sintering and densification of magnesium aluminum spinel[J]. Journal of Kunming University of Science and Technology (Natural Sciences), 2021, 46(4): 11-17 (in Chinese).
[88] 张培培. MgAl₂O₄透明陶瓷的凝胶注成型及其性能研究[D]. 徐州: 江苏师范大学, 2016.
ZHANG P P. Gel casting of MgAl₂O₄ transparent ceramics and its properties[D].Xuzhou: Jiangsu Normal University, 2016 (in Chinese).
[89] 王操, 孟志新, 成来飞, 等. 放电等离子烧结技术制备MgAl₂O₄透明陶瓷的研究进展[J]. 材料导报, 2009, 23(S1): 373-374+380.
WANG C, MENG Z X, CHENG L F, et al. Research progress in transparent MgAl₂O₄ ceramics fabricated by spark plasma sintering[J]. Materials Review, 2009, 23(S1): 373-374+380 (in Chinese).
[90] YOSHIDA H, BISWAS P, JOHNSON R, et al. Flash-sintering of magnesium aluminate spinel (MgAl₂O₄) ceramics[J]. Journal of the American Ceramic Society, 2017, 100(2): 554-562.
[91] SOKOL M, HALABI M, MORDEKOVITZ Y, et al. An inverse Hall-Petch relation in nanocrystalline MgAl₂O₄ spinel consolidated by high pressure spark plasma sintering (HPSPS)[J]. Scripta Materialia, 2017, 139: 159-161.
[92] TAKAHASHI S, KAN A, OGAWA H. Microwave dielectric properties and crystal structures of spinel-structured MgAl₂O₄ ceramics synthesized by a molten-salt method[J]. Journal of the European Ceramic Society, 2017, 37(3): 1001-1006.
[93] IQBAL M J, ISMAIL B, RENTENBERGER C, et al. Modification of the physical properties of semiconducting MgAl₂O₄ by doping with a binary mixture of Co and Zn ions[J]. Materials Research Bulletin, 2011, 46(12): 2271-2277.
[94] ZATSEPIN A F, KIRYAKOV A N, ZATSEPIN D A, et al. Modification of MgAl₂O₄ electron-optic properties by pulsed ion beam[J]. Physics of Atomic Nuclei, 2019, 82(11): 1558-1564.
[95] OSIPOV V V, IL’ICHEV N N, SHITOV V A, et al. Fabrication and characterization of highly transparent Fe²⁺∶MgAl₂O₄ ceramics[C]//Proc SPIE 11322, XIV International Conference on Pulsed Lasers and Laser Applications, 2019, 11322: 135-142.
[96] SYED N Q, SHYAM S B, GUILLERMO V A, et al. Spinel Optics for High Energy Lasers[C]. Proc. SPIE, 10985: 1098508-10.
[97] SANGHERA J, BAYYA S, VILLALOBOS G, et al. Transparent ceramics for high-energy laser systems[J]. Optical Materials, 2011, 33(3): 511-518.
[98] 韩丹.镁铝尖晶石透明陶瓷的制备与性能研究[D]. 上海: 中国科学院上海硅酸盐研究所, 2018.
HAN D. Preparation and properties of transparent spinel ceramics[D]. Shanghai: Shanghai Institute of Ceramics,Chinese Academy of Sciences, 2018 (in Chinese).
[99] 荆延秋, 刘强, 苏莎, 等. 1.5 μm被动调Q可饱和吸收体用Co∶MgAl₂O₄透明陶瓷的制备[J]. 无机材料学报, 2021, 36(8): 877-882.
JING Y Q, LIU Q, SU S, et al. Fabrication of highly transparent Co∶MgAl₂O₄ ceramic saturable absorber for passive Q-switching at 1.5 μm[J]. Journal of Inorganic Materials, 2021, 36(8): 877-882 (in Chinese).
[100] 袁泽, 王皓, 涂兵田, 等. MgO·1.5Al₂O₃透明陶瓷的无压/热等静压烧结制备[J]. 无机材料学报, 2015, 30(8): 843-847.
YUAN Z, WANG H, TU B T, et al. Preparation of MgO·1.5Al₂O₃ transparent ceramic by pressureless sintering and hot isostatic pressing[J]. Journal of Inorganic Materials, 2015, 30(8): 843-847 (in Chinese).
[101] 张亚倩, 张荣实, 王跃忠, 等. 超细镁铝尖晶石凝胶注模成型工艺研究[J]. 陶瓷学报, 2020, 41(1): 52-57.
ZHANG Y Q, ZHANG R S, WANG Y Z, et al. Gelcasting process of ultra-fine magnesia alumina spinel[J]. Journal of Ceramics, 2020, 41(1): 52-57 (in Chinese).
[102] 杨勇, 商青琳, 李特, 等. 热处理对铝酸镁尖晶石透明陶瓷性能的影响[J]. 稀有金属材料与工程, 2015, 44(增刊): 105-108.
YANG Y, SHANG Q L, LI T, et al. Effects of heat treatment on spinel ceramic microstructure and optical transmittance[J]. Rare Metal Materials and Engineering, 2015, 44(supplyment): 105-108 (in Chinese).
[103] 程艳玲, 于浩海, 张怀金, 等. 自倍频晶体的研究和激光应用进展[J]. 应用技术学报, 2021, 21(2): 95-108.
CHENG Y L, YU H H, ZHANG H J, et al. Research and laser application progress of self-frequency doubling crystal[J]. Journal of Technology, 2021, 21(2): 95-108 (in Chinese).
[104] 苏莎. Co∶MgAl₂O₄透明陶瓷的微结构调控和性能优化[D]. 镇江: 江苏大学, 2019.
SU S. Microstructure control and performance optimization of Co∶MgAl₂O₄ transparent ceramics[D].Zhenjiang: Jiangsu University, 2019 (in Chinese).
[105] 彭星淋, 李淑星, 刘泽华, 等. 大功率固态照明用荧光陶瓷研究进展[J]. 无机材料学报, 2021, 36(8): 807-819.
PENG X L, LI S X, LIU Z H, et al. Phosphor ceramics for high-power solid-state lighting[J]. Journal of Inorganic Materials, 2021, 36(8): 807-819 (in Chinese).
[106] 福建中科芯源光电科技有限公司. K-COB解读[EB/OL].[2023-09-21]. https://www.k-cob.com/h-col-121.html.
Fujian Zhongkexinyuan photoelectric technology Co., LTD. K-cob interpretation[EB/OL].[2023-09-21]. https://www.k-cob.com/h-col-121.html (in Chinese).
[107] 许传龙, 严祥生, 陈宗煜, 等. 透明荧光陶瓷LED隧道灯在瑞寻高速公路中的应用[J]. 中国交通信息化, 2023(S1): 393-396.
XU C L, YAN X S, CHEN Z Y, et al. Application of transparent fluorescent ceramic LED tunnel lamp in Ruixun Expressway[J]. China ITS Journal, 2023(S1): 393-396 (in Chinese).