拉晶工艺参数对N型单晶硅氧含量的影响研究

摘要/Abstract

摘要： TOPCon电池基板是以N型硅片为主,N型硅片的氧含量在一定程度上影响着TOPCon电池的转换效率。本文采用直拉法进行单晶硅的拉制,通过调整埚转、氩气流量和炉压来研究拉晶工艺参数对N型单晶硅氧含量的影响。数值模拟分析和实验结果表明:坩埚转速的增加会抑制浮力-热毛细漩涡,减少熔体界面处SiO的挥发,提高硅熔体内部和单晶硅棒氧含量;增大氩气流量和降低炉压可增大熔体界面处SiO的质量流量,有效促进SiO挥发,减少固液界面处氧含量,从而降低单晶硅棒氧含量。根据单晶硅氧含量测试和EL检测结果可知,坩埚转速5 r/min、氩气流量100 L/min和炉压1 200 Pa时拉制的N型单晶硅氧含量最低,电池端同心圆比例也是最低的。本文研究结果可为N型单晶硅棒降氧提供一定思路。

关键词: N型单晶硅, 降氧, 坩埚转速, 氩气流量, 炉压, 同心圆

Abstract: TOPCon cell substrates are dominated by N-type silicon wafers, and the oxygen content of N-type silicon wafers affects the conversion efficiency of TOPCon cells to a certain extent. In this paper, the Czochralski method was used to grow monocrystalline silicon, and the influence of crystal growth process parameters on the oxygen content of N-type monocrystalline silicon were studied by adjusting the crucible rotation rates, argon flow rates and furnace pressure. The numerical simulation analysis and experimental results show that: the accretion of crucible rotation rates can suppress buoyancy-thermal capillary vortices, reduce the volatilization of SiO at the melt interface, and increase the oxygen content in the silicon melt and in the monocrystalline silicon rods; increasing the argon flow rates and decreasing the furnace pressure can enlarge the mass flow rates of SiO at the melt interface, effectively promote SiO volatilization, reduce the oxygen content at the solid-liquid interface, and thus lessen the oxygen content in the monocrystalline silicon rods. The monocrystalline silicon oxygen content test and EL detection results show that, with the 5 r/min of crucible rotation rate, 100 L/min of argon flow rate, and 1 200 Pa of furnace pressure, the oxygen content in N-type monocrystalline silicon is the lowest, and the concentric circle ratio is also the lowest in the production of photovoltaic cells. The research in this paper can provide some ideas for reducing oxygen content in N-type monocrystalline silicon rods.

Key words: N-type monocrystalline silicon, reduction of oxygen content, crucible rotation rate, argon flow rate, furnace pressure, concentric circle

中图分类号:

O782

柴晨, 张军, 王玉龙, 韩庆辉, 李怀铭. 拉晶工艺参数对N型单晶硅氧含量的影响研究[J]. 人工晶体学报, 2024, 53(5): 792-802.

CHAI Chen, ZHANG Jun, WANG Yulong, HAN Qinghui, LI Huaiming. Research on the Influence of Czochralski Process Parameters on Oxygen Content of N-Type Monocrystalline Silicon[J]. JOURNAL OF SYNTHETIC CRYSTALS, 2024, 53(5): 792-802.

参考文献

[1] FELDMANN F, BIVOUR M, REICHEL C, et al. Passivated rear contacts for high-efficiency n-type Si solar cells providing high interface passivation quality and excellent transport characteristics[J]. Solar Energy Materials and Solar Cells, 2014, 120: 270-274.
[2] CHEN Y, CHEN D, ALTERMATT P P, et al. >25% large area industrial silicon solar sell: learning from history and future perspective[C]//Marseille, France: 36th EU PVSEC, 2019.
[3] GREEN M A, DUNLOP E D, LEVI D H, et al. Solar cell efficiency tables (version 54)[J]. Progress in Photovoltaics: Research and Applications, 2019, 27(7): 565-575.
[4] 白宇, 何佳龙, 李君君, 等. 光电性能可调的TiN薄膜及在TOPCon太阳电池的应用[J]. 太阳能学报, 2023, 44(9): 72-77.
BAI Y, HE J L, LI J J, et al. Tin thin film with adjustable photoelectric performance and its application in topcon solar cell[J]. Acta Energiae Solaris Sinica, 2023, 44(9): 72-77 (in Chinese).
[5] 钱金忠, 左克祥, 王安, 等. TOPCon太阳电池中多晶硅层磷掺杂工艺的优化及其对电性能的影响[J]. 太阳能, 2023, 353(9): 54-59.
QIAN J Z, ZUO K X, WANG A, et al. Optimization of phosphorus doping process for poly-Si layer in TOPCon solar cells and ITS effect on electrical performance[J]. Solar Energy, 2023, 353(9): 54-59.
[6] 魏凯峰, 刘大伟, 倪玉凤, 等. N型TOPCon晶硅太阳能电池光注入退火增效的研究[J]. 人工晶体学报,2021, 50(1): 66-72.
WEI K F, LIU D W, NI Y F, et al. Light injection study of N-TOPCon silicon solar cells on annealing synergies[J]. Journal of Synthetic Crystals, 2021, 50(1): 66-72.
[7] LOHMÜLLER E, LOHMÜLLER NÉE WERNER S, WÖHRLE N, et al. BBr₃ diffusion with second deposition for laser-doped selective emitters from borosilicate glass[J]. Solar Energy Materials and Solar Cells, 2018, 186: 291-299.
[8] LI M J, WONG J, WANG E C, et al. Predictive simulation framework for boron diffused p+ layer optimization: sensitivity analysis of boron tube diffusion process parameters of industrial n-type silicon wafer solar cells[J]. Solar Energy Materials and Solar Cells, 2019, 189: 63-74.
[9] 李继阳. 光伏用直拉硅中氧相关缺陷的研究[D]. 杭州: 浙江大学, 2018.
LI J Y. Study of oxygen-related defects in Czochralski silicon used for photovoltaics[D]. Hangzhou: Zhejiang University, 2018.
[10] 刘建华, 龙辉, 李程, 等. TOPCon电池低压硼扩散设备的发展趋势分析[J]. 电子工业专用设备, 2023, 52(1): 1-6+59.
LIU J H, LONG H, LI C, et al. The development trend analysis of TOPCon battery low boron diffusion equipment[J]. Equipment for Electronic Products Manufacturing, 2023, 52(1): 1-6+59 (in Chinese).
[11] 刘世龙, 黄旭光, 李卫涛, 等. N型直拉单晶中硅的同心圆缺陷分析[C]//第十八届中国太阳能级硅及光伏发电研讨会, 2022.
LIU S L, HUANG X G, LI W T, et al. Concentric circle defect analysis of silicon in N-type czochralski single crystal[C]//18th China SoG Silicon and PV Power Conference, 2022.
[12] 付楠楠. 单晶硅片同心圆现象产生及影响研究[C]//第十八届中国太阳能级硅及光伏发电研讨会, 2022.
FU N N. Study on the formation and influence of concentric circle phenomenon of monocrystalline silicon[C]//18th China SoG Silicon and PV Power Conference, 2022.
[13] 张梦宇. 大尺寸直拉法单晶硅生长过程的控氧研究[D]. 昆明: 昆明理工大学, 2023.
ZHANG M Y. Oxygen control study of large-sized single crystal silicon in the growth process of Czochralski[D]. Kunming: Kunming university of science and technology, 2023.
[14] 潘国刚, 胡玮芳, 何火军. 硅单晶片中的氧及对后续缺陷的影响[J]. 微电子学, 2019, 49(1): 140-145.
PAN G G, HU W F, HE H J. Effects of oxygen content on defects in silicon wafer[J]. Microelectronics, 2019, 49(1): 140-145 (in Chinese).
[15] 高农农, 葛林. 加热器直径对200 mm太阳能级单晶硅加热效率、能耗和氧含量的影响[J]. 硅酸盐通报, 2015, 34(12): 3658-3661.
GAO N N, GE L. Influence of heater diameter on heating efficiency, power consumption and oxygen concentration in the solar-grade single silicon[J]. Bulletin of the Chinese Ceramic Society, 2015, 34(12): 3658-3661.
[16] 李进, 张洪岩, 高忙忙, 等. 氩气流速对400 mm大直径磁场直拉单晶硅固液界面、热应力及氧含量的影响[J]. 人工晶体学报, 2014, 43(5): 1193-1198.
LI J, ZHANG H Y, GAO M M, et al. Influence of argon flow rate on the solid / liquid interface, thermal stress and oxygen concentration in the 400 mm CZ silicon with a magnetic field[J]. Journal of Synthetic Crystals, 2014, 43(5): 1193-1198 (in Chinese).
[17] 吴明明, 周标. 直拉单晶硅体生长过程中的控氧技术研究[J]. 新技术新工艺, 2013, 11: 98-101.
WU M M, ZHOU B. Research on oxygen control technology in Czochralski single crystal silicon growth[J]. New technologies and processes, 2013, 11: 98-101.
[18] 杨露, 宋志成, 倪玉凤, 等. TOPCon太阳能电池选择性发射极工艺研究[J]. 人工晶体学报, 2024, 53(1): 138-144.
YANG L, SONG Z C, NI Y F, et al. Process study on selective emitter of TOPCon solar cells[J]. Journal of Synthetic Crystals, 2024, 53(1): 138-144 (in Chinese).
[19] 芮阳, 王忠保, 盛旺, 等. 热屏结构对 200 mm半导体级提拉单晶硅中氧含量分布的影响[J]. 人工晶体学报, 2023, 52(6): 1110-1119.
RUI Y, WANG Z B, SHENG W, et al. Effect of heat shield structure on the distribution of oxygen content in 200 mm semiconductor-grade Czochralski monocrystalline silicon[J]. Journal of Synthetic Crystals, 2023, 52(6): 1110-1119.
[20] CHEN J C, CHIANG P Y, NGUYEN T H T, et al. Numerical simulation of the oxygen concentration distribution in silicon melt for different crystal lengths during Czochralski growth with a transverse magnetic field[J]. Journal of Crystal Growth, 2016, 452: 6-11.
[21] 刘立军. 晶体生长数值模拟领域的若干研究进展[J]. 中国材料进展, 2019, 38(5): 523-527.
LIU L J. Some research progress in the field of numerical simulation of crystal growth[J]. Materials China, 2019, 38(5): 523-527 (in Chinese).
[22] JOMÂA M, M’HAMDI M, HU Y, et al. Numerical analysis of oxygen control during growth of Czochralski silicon single crystals[C]//2014 IEEE 40th Photovoltaic Specialist Conference (PVSC). Denver, CO, USA. IEEE, 2014: 3521-3525.
[23] 夏中高, 彭平, 景彦姣, 等. EL检测PERC电池中间缺陷成因及改善方法的研究[J]. 太阳能学报, 2023, 44(6): 198-203.
XIA Z G, PENG P, JING Y J, et al. Study on causes and improvement methods of intermediate defects in perc cells detected by EL[J]. Acta Energiae Solaris Sinica, 2023, 44(6): 198-203 (in Chinese).
[24] STR Group. CGSim Flow Module Theory Manual[EB/OL]. [2013-01-24].https://www.docin.com/p-589665499.html.
[25] NGUYEN T H T, CHEN J C, HU C, et al. Effects of crystal-crucible iso-rotation and a balanced/unbalanced cusp magnetic field on the heat, flow, and oxygen transport in a Czochralski silicon melt[J]. Journal of Crystal Growth, 2020, 531: 125373.
[26] 刘东林. 浅析如何降低单晶硅棒头部的氧含量[J]. 中国科技纵横, 2014(21): 53-54.
LIU D L. How to reduce the oxygen content at the head of a single crystal silicon rod[J]. China Science & Technology Overview, 2014(21): 53-54.
[27] 王黎光, 芮阳, 盛旺, 等. 横向磁场下坩埚转速对半导体级直拉单晶熔体中流场与氧浓度的影响机制[J]. 人工晶体学报, 2023, 52(9): 1641-1650.
WANG L G, RUI Y, SHENG W, et al. Influence mechanism of crucible rotation rates on the flow field and oxygen concentration of the semiconductor-grade Czochralski monocrystalline silicon melt under transverse magnetic field[J]. Journal of Synthetic Crystals, 2023, 52(9): 1641-1650.